牌号简介 About |
---|
Magnum*3904是一种挤出/热成型树脂,开发用于高冲击和其他技术应用。质量(连续加工)的ABS技术确保了一个ABS树脂,结合了良好的加工性能和稳定的光基色,是理想的自我着色。由于其微粒含量极低,该等级是“平滑系列”的一个补充,具有较低的板(LP)出含量。这导致了一个优越的表面光洁度,在这一点上,挤出机辊组上的板料堆积显著减少。这一新级别使客户能够以较低的总成本生产具有卓越美学和表面清洁度的零件。应用汽车室内家具 MAGNUM* 3904 is an extrusion / thermoforming resin developed for high impact and other technical applications. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base colour that is ideal for self-colouring. With its ultra-low particulate content, this grade is an addition to the " Smooth Series" and features a lower plate (LP) out content. This results in a superior surface finish in which the plate out build-up on the extruder roll stack is reduced significantly. This new grade enables customers to produce parts with both outstanding aesthetics and surface cleanness at lower total cost. Applications Automotive interior Furniture |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 | g/cm³ | ISO 1183/B |
表观密度 Apparent density |
0.65 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
220℃,10.0kg 220℃,10.0kg |
4.7 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.10 to 0.70 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
1820 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
MPa | ISO 527-2/50 | |
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
MPa | ISO 527-2/100 | |
拉伸应变 Tensile strain |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
% | ISO 527-2/50 | |
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
% | ISO 527-2/100 | |
弯曲模量 Bending modulus 2 , 3 |
MPa | ISO 178 | |
弯曲强度 bending strength 2 , 3 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 5 |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 3 点 |
4 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
5 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
【新闻资讯】查看全部
朗盛在中国的投资脚步没有停歇 加码新资料
2015-12-29 一家被“抛弃”的企业,如何做到十年翻一番? 化工行业极其频繁的兼并重组,一方面造就了“陶氏+杜邦”的巨无霸,另一方面,那些被剥离的企业却不得不面对日益残酷的市场经营环境。 2004年,从拜耳集团剥离出来的朗盛,就走到了这样的十字路口。朗盛大中华区总裁钱明诚在接受《英才》记者专访时坦言,“刚从拜耳分割出来,走了一些弯道路,当时有一些合资的企业不是很成功,对合资比较谨慎,步伐比较缓慢。” 而十年后,通过整合重组, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |