牌号简介 About |
---|
释放膜双向拉伸聚丙烯(BOPP)膜与表面聚合物共挤出两侧。RGR03/120是一系列专为各种工业应用而设计的释放膜的一部分。 Release Film Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with surface polymers. RGR03/120 is part of a family of release films that are designed for use in a range of industrial applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
收缩率 Shrinkage rate |
|||
MD:129℃,1 min MD:129℃,1 min |
6.0 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态,外层/外层 With oneself - dynamic, outer/outer layers |
0.25 | ASTM D1894 | |
与自身 - 静态,外层/外层 Compared to itself - static, outer/outer layers |
0.35 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
3000 | µm | |
割线模量 Secant modulus 2 |
ASTM D882 | ||
1% 正割,MD 1% secant, MD |
2300 | MPa | ASTM D882 |
1% 正割,TD 1% secant, TD |
MPa | ASTM D882 | |
拉伸强度 tensile strength 3 |
ASTM D882 | ||
MD,屈服 MD, yield |
MPa | ASTM D882 | |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 3 |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
用量 dosage |
m²/kg | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10%/min |
3 50%/min |
【新闻资讯】查看全部
宜丰国轩碳酸锂项目开工
2022-01-08 搜料网资讯: 2021年12月29日,宜丰国轩锂业项目在江西省宜丰县正式破土动工。 据悉,宜丰国轩锂业有限公司是宜春国轩锂业股份有限公司全资子公司,计划建成年产5万吨电池级碳酸锂 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |