| 牌号简介 About |
|---|
| Styrolux® T是一种新的开发、透明和坚韧的丁苯共聚物（SBC），专门为高性能薄膜挤出和收缩薄膜应用而设计。Styrolux® T已开发用于与第二个SBC组件Styrolux S混合，该组件可增加膜的刚度并提高膜卷的存储稳定性（减少自然收缩）。具有优异的清晰度和韧性，最大收缩率达到80%，非常好的收缩控制，非常低的凝胶含量。 Styrolux® T is a new developmental, clear and tough styrene-butadiene copolymer (SBC) designed specifically for high performance film extrusion and shrink film applications. Styrolux® T has been developped for blending with a second SBC component, Styrolux® S, which inceases the stiffness of the film and improves the storage stability of film reels (reduced natural shrinkage). FEATURES Excellent clarity and toughness Maximum shrinkage up to 80% Very good shrinkage control Very low gel content APPLICATIONS Blend component for Styrolux S Shrink sleeve applications Label film |
产品描述 Product Description
用途：薄膜;标签;收缩性薄膜;混合;
颜色：清晰/透明
加工条件：薄膜挤出 Film extrusion
性能特点： 嵌段共聚物; 低速凝固晶点; 透光性好; 韧性好; 收缩性高; Good Clarity,Good flexibility,Low speed solidification point,Block Copolymer,High shrinkage
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
200℃，5.0kg 200℃，5.0kg |
10 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
200℃，5 kg 200℃，5 kg |
11.0 | cm³/10min | ISO 1133 |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
0.070 | % | ISO 62 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
60 | ASTM D2240 | |
|
邵氏 D Shaw's D |
67 | ISO 868 | |
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
|||
|
屈服，23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
|
屈服，23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
屈服，23℃ Yield, 23 ℃ |
% | ASTM D638 | |
|
屈服，23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
|
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
|
23℃ 23℃ |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
ISO 179 | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
B50 B50 |
℃ | ISO 306 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
透光率 Transmittance |
|||
|
550 nm 550 nm |
% | ASTM D1003 | |
|
雾度 Haze |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 标准 B (120°C/h), 压 力1 (10N) |
|
【新闻资讯】查看全部 
CRP公司推出新款高弹性3D打印资料Windform RL
2017-03-29 CRP科技公司近日推出了一款新的3D打印材料Windform RL。它是该公司专业级3D打印材料系列Windform的首款热塑性弹性体材料，具有优异的弹性、稳定性、耐用性和机械性能，所以十分适用于打印复杂的几何形状，以及对柔韧性有高要求的应用，如减震部件。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付