牌号简介 About |
---|
Styrolux® 684D是一种透明的苯乙烯-丁二烯共聚物(SBC),用于增强韧性的零件的注射成型,以及片材和薄膜挤出和吹塑成型。Styrolux® 684D制成的零件显示出优异的印刷性能。特点:高清晰度、高韧性、良好的印刷性、高透气性、符合水蒸气法规的应用、食品包装容器、杯子和盖子、玩具、挤压片和薄膜医疗设备 Styrolux® 684D is a clear styrene-butadiene copolymer (SBC) used in injection molding for parts with enhanced toughness as well as in sheet and film extrusion and blow molding. Parts made of Styrolux® 684D reveal excellent printability. FEATURES High clarity Improved toughness Good printability High permeability to gases and water vapor Regulatory compliant APPLICATIONS Food packaging Container, cups and lids Toys Extruded sheet and thin film Medical devices |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.01 | g/cm³ | ASTM D792 |
密度 Density |
1.01 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
11 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
200℃,5 kg 200℃,5 kg |
11.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.30 to 1.0 | % | ISO 294-4 |
MD MD |
% | ASTM D955 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
饱和,23℃ Saturation, 23 ℃ |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弹性模量 Elastic modulus |
|||
TD TD |
MPa | ASTM D882 | |
MD MD |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
MD,断裂 MD, fracture |
% | ISO 527-3 | |
MD,断裂 MD, fracture |
% | ASTM D882 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD MD |
g | ASTM D1922 | |
撕裂强度 tear strength |
|||
TD TD |
g | ASTM D1922 | |
氧气传输速率 Oxygen transfer rate |
|||
23℃,0% RH 23℃,0% RH |
cm³/m²/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance 2 |
|||
23℃ 23℃ 2 |
g/m²/24 hr | ASTM F1249 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
ISO 179 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ |
kJ/m² | ISO 180-A | |
23℃ 23℃ |
kJ/m² | ISO 180-A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
Peak force Peak force |
J | ASTM D3763 | |
Total energy Total energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed 3 |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed 3 |
℃ | ISO 75-2/B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
MD MD |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电常数 Dielectric constant |
|||
100 Hz 100 Hz |
IEC 60250 | ||
1.00 mm,1 MHz 1.00 mm,1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index 5 |
ASTM D542 | ||
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
|||
550 nm 550 nm |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0% to 85% RH gradient |
3 4h/80°C |
4 标准 B (120°C/h), 压 力1 (10N) |
5 Sodium D Line |
【新闻资讯】查看全部
比起战争,市场更怕的是全球经济衰退
2022-03-01 随着俄乌危机全面爆发,全球市场不断跌宕起伏,市场在分析标普500指数的修正幅度时指出,今年已经出现了与过去33次平均15%修正幅度一样的跌幅,全球或将进入经济衰退更让市场担 |
比起战争,市场更怕的是全球经济衰退 随着俄乌危机全面爆发,全球市场不断跌宕起伏,市场在分析标普500指数的修正幅度时指出,今年已经出现了与过去33次平均15%修正幅度一样的跌幅,全球或将进入经济衰退更让市场担忧。 虽然在俄乌冲突全面爆发之际,上周五科技股连续两日反弹,道指涨超830点创15个月最大涨幅,标普纳指止步两周连跌涨超2%,纳指涨1.6%;但面对或将出现的全球经济衰退,发达国家股票市场可能将有“无法承受之重”了。 周末,欧美各国对俄罗斯实施了更严厉制裁,将包括俄央行等部分俄主要银行从SWIFT信息系统剔除,并将俄罗斯央行的外汇储备作为攻击目标。而俄罗斯也采取了反击,包括俄央行将关键利率提升至20%、释放7330亿卢布缓冲、禁止外国人抛售、强制售汇、推迟市场开盘等一系列资本管制“组合拳”。 尽管周一国际原油小幅下挫,但继续飙升的原油趋势以及收益率曲线预示着市场对经济增长的担忧不断增加;叠加美元飙升以及流动性紧缩预期上升,各经济体的压力正在升温。如果经济未来迎来全面衰退,那么股票市场将更难保持弹性。 俄乌这场自1945年二战结束以来欧洲最严重的冲突或产生极其严重后果,即随着能源价格继续飙升,全球经济很容易陷入三年内的第二次衰退: 俄罗斯作为欧洲石油和天然气的主要供应国,直接的冲击便是大宗商品市场:欧洲天然气期货价格飙升,能源行业正面临供应中断的局面;油价也突破100美元/桶,达到2014年以来的最高水平。 在石油和天然气继续流动的情况下,美国的通货膨胀可能继续推高,彭博分析称一旦能源供应中断,可能会将美国3月份的通胀率推高至9%,并在年底前保持在接近6%的水平。 虽然目前金融市场还未出现股票抛售,债券收益率下降信用利差并未扩大很多,但是眼下有序的金融市场可能会面临企业和消费者严重丧失信心从而导致更大规模的冲突。 这场危机或将增加各国央行提高利率的压力,也就意味着宏观经济风险依然存在。 彭博社引援MKM Partners的首席市场技术人员JC O‘Hara的观点,其认为正确的判断可能是标准普尔500指数下跌36%,即熊市的平均跌幅后出现反弹。 MKM研究了标普500的33次修正,其将标普500从收盘高点下跌10%定义为修正。其中,7次达到了熊市定义,即下跌20%;其余26次则在下跌后反弹并达到了新高。平均15%的修正幅度也与从今年1月4日到2月24日盘中低点的14.6%跌幅一致。 MKM进一步表示,如果经济不会进入衰退期,那么市场的低点就应该或多或少地进入。 如果我们没有进入经济衰退,我们应该使用结构性牛市里面的修正的游戏规则。 Stifel股票策略师Barry Bannister则表示,自1962年以来,已经有17次非衰退期的标普500指数调整超过10%,平均跌幅为16.95%,因此他现在认为该指数的底线为4050点,即比1月初的创纪录收盘价下跌约15%。 Miller Tabak的首席市场策略师Matt Maley更是直接表示称: 经济衰退很可能在今年的某个时候开始。我们正在走向熊市。 美国股票期货周一暴跌多达2.9%,抹去了上周末的涨幅,市场预期各国央行或将放缓紧缩政策的猜测使得俄乌危机影响全球经济增长的担忧略有减缓。截止发文,标普500跌幅从隔夜近3%的跌幅收窄至0.11%。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |