牌号简介 About |
---|
Centrene® HDF193N是一种无色素的高分子量双峰高密度聚乙烯。HDF193N含有抗氧化剂,以保护它在挤压和最终使用 。Centrene® HDF193N是一种基础树脂,用于需要高密度PE100型树脂的管道剥离和夹套化合物。如果预期的应用涉及间歇性到长时间暴露在阳光下,则应考虑添加紫外线稳定剂。应通过适当的性能测试来确定在任何应用中的适用性。 Alkadyne HDF193N is a non-pigmented high molecular weight bimodal High Density Polyethylene. Alkadyne HDF193N contains antioxidants to protect it during extrusion and end use. Alkadyne HDF193N has been designed as a base resin for pipe striping and jacket compounds where High Density PE100 Type resin is required. Addition of a UV stabilizer should be considered where the intended application involves intermittent to extended exposure to sunlight. Suitability for use in any application should be determined by appropriate performance testing. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.948 | g/cm³ | 内部方法 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,21.6kg 190℃,21.6kg |
8.9 | g/10min | ASTM D1238 |
190℃,5.0kg 190℃,5.0kg |
0.31 | g/10min | ASTM D1238 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
氧感应时间 Oxygen sensing time |
|||
210℃ 210℃ |
> 20 | min | ISO 11357-6 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Pipe Stress Rupture(5.4 MPa,80℃) Pipe Stress Rupture(5.4 MPa,80℃) |
> 6.9 | day | AS/NZS 1462.6 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
研讨称黑色素能让塑料拥有更强功能
2016-11-14 如果你想要更耐用持久的塑料泡沫或纺织品,答案可能存在于你的皮肤、头发或眼睛中。现在科学家利用天然存在于人体及其它动物身上的黑色素来使塑料拥有更强性能。 据外媒报道,中国江南大学的科学家已经确定,在聚氨酯中添加少量黑色素后,可以使其性能变得更强。 在实验室测试中,由江南大学研究人员陈明清和东为富尝试从乌贼墨囊中提取黑色素,并将其添加到普通的液态聚氨酯中。 研究人员表示,即使最终固化得到的聚氨酯泡沫中仅增加了百分之二的黑色素,但结果显示其韧性是普 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |