| 牌号简介 About |
|---|
| ELITE™ AT 6101增强聚乙烯树脂是一种通过陶氏原位技术生产的共聚物。它设计用于拉伸蹄子应用，并提供了一个独特的结合的保持力，弹性恢复，光学和韧性。主要特点：优良的弹性恢复和保持力、极高的抗冲击性和撕裂性能、易加工性符合：美国FDA 21 CFR 175.105（c）（5）欧盟，2011年10月，详细信息请参考法规。 ELITE™ AT 6101 Enhanced Polyethylene Resin is a copolymer produced via INSITE™ technology from Dow. It is designed for stretch hooder application and offers a unique combination of holding force, elastic recovery, optics and toughness. Main Characteristics: Excellent elastic recovery and holding force Very high impact resistance and tear properties Ease of processing Complies with: U.S. FDA 21 CFR 175.105(c)(5) EU, 10/2011 Consult the regulations for complete details. |
产品描述 Product Description
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.905 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.80 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
25 | µm | |
|
膜刺穿强度 Membrane puncture strength |
5.65 | J | 内部方法 |
|
膜刺穿力 Membrane puncture force |
57.8 | N | 内部方法 |
|
膜耐刺穿性 Membrane puncture resistance |
J/cm³ | 内部方法 | |
|
膜强度 Membrane strength |
ASTM D882 | ||
|
MD MD |
J/cm³ | ASTM D882 | |
|
TD TD |
J/cm³ | ASTM D882 | |
|
割线模量 Secant modulus |
ASTM D882 | ||
|
1% 正割，MD 1% secant, MD |
MPa | ASTM D882 | |
|
2% 正割，MD 2% secant, MD |
MPa | ASTM D882 | |
|
1% 正割，TD 1% secant, TD |
MPa | ASTM D882 | |
|
2% 正割，TD 2% secant, TD |
MPa | ASTM D882 | |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
MD，屈服 MD, yield |
MPa | ASTM D882 | |
|
TD，屈服 TD, yield |
MPa | ASTM D882 | |
|
MD，断裂 MD, fracture |
MPa | ASTM D882 | |
|
TD，断裂 TD, fracture |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
MD，断裂 MD, fracture |
% | ASTM D882 | |
|
TD，断裂 TD, fracture |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact |
g | ASTM D1709B | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength 2 |
ASTM D1922 | ||
|
MD MD |
g | ASTM D1922 | |
|
TD TD |
g | ASTM D1922 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | 内部方法 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45° 45° |
ASTM D2457 | ||
|
雾度 Haze |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 方法 B |
|
【新闻资讯】查看全部 
印尼国家石油公司预计出现爆炸的巴隆甘炼油厂将于4-5天内重启
2021-03-30 搜料网资讯： 印尼国家石油公司一名官员表示，预计将在4至5天内重启其位于西爪哇巴隆甘的12.5万桶/日的炼油厂，该厂于29日凌晨发生爆炸并产生火灾，导致生产作业紧急关闭。 印尼国 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付