PRE-ELEC® ESD 7100是一种基于ABS的静态耗散热塑性化合物。耗散性是永久性的,并嵌入到聚合物链中。PRE-ELEC® ESD 7100已开发用于注塑和挤出热成型单层或多层片材。由PRE-ELEC® ESD 7100制成的产品是可清洗、可重复使用和可回收的。表面电阻值为1E8欧姆(EOS/ESD S11.11-1993,IEC 61340-5-1),可通过最佳工艺参数实现。典型应用包括托盘、手提箱、板条箱和技术部件,它们为电子、医疗、制药和纸张处理行业提供永久性的静电放电保护。PRE-ELEC® ESD 7100可以着色成各种明亮的颜色。 PRE-ELEC® ESD 7100 is a static dissipative thermoplastic compound based on ABS. The dissipative property is permanent and built into the polymer chain. PRE-ELEC® ESD 7100 has been developed for injection moulding and for the extrusion of thermoformable mono- or multi-layer sheet. The products made out of PRE-ELEC® ESD 7100 are washable, reusable and recyclable. Surface resistance values of 1e8 ohms (EOS/ESD S11.11-1993, IEC 61340-5-1) can be achieved with optimum processing parameters. Typical applications include trays, tote bins, crates and technical parts which give permanent ESD protection for the electronics, medical, pharmaceutical and paper handling industries. PRE-ELEC® ESD 7100 can be coloured into various bright colours. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ASTM D792 |
密度 Density |
1.07 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
200℃,21.6kg 200℃,21.6kg |
20 | g/10min | ISO 1133 |
200℃,5.0kg 200℃,5.0kg |
5.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.50 to 0.70 | % | ISO 294-4 |
MD MD |
% | ASTM D955 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ASTM D638 | |
4 mm 4 mm |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,4 mm Fracture, 4 mm |
% | ISO 527-2 | |
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
4 mm 4 mm |
MPa | ASTM D790 | |
4 mm 4 mm |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 2 |
ISO 180 | ||
Area Area |
ASTM D256 | ||
-20℃,4.00 mm -20℃,4.00 mm |
kJ/m² | ASTM D256 | |
23℃,4.00 mm 23℃,4.00 mm |
kJ/m² | ASTM D256 | |
-20℃ -20℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D256 | ||
-20℃,4 mm -20℃,4 mm |
kJ/m² | ASTM D256 | |
23℃,4 mm 23℃,4 mm |
kJ/m² | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 2 |
ISO 180 | ||
-20℃ -20℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648-B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 3 | |
A50 A50 |
℃ | ISO 306/A50 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ESD STM11.11 | |
表面电阻率 Surface resistivity |
ohms | IEC 61340-2-3 | |
静电衰减 Electrostatic attenuation |
|||
-- -- |
sec | ESD S20.20 | |
-- -- |
sec | IEC 61340-5-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 4 mm thickness |
3 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
4月份全国煤炭行业运行态势
2021-05-01 搜料网资讯: [导语]:4月国内煤市运行主要特点:国内煤炭供应整体偏紧,一季度煤炭进口量同比下降明显,秦皇岛港煤炭库存低位水平震荡运行,全社会用电量持续回升。 动力煤方面 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |