牌号简介 About |
---|
旭化成Tuftec™ H1062是为聚丙烯(PP)抗冲击改性剂而设计的。它提供了良好的性能平衡,可以提高室温和低温下的抗冲击性能。H1062可作为增强聚丙烯薄膜热封性的添加剂。用途:主要用作汽车内饰和内饰用聚丙烯的改性剂。也可用作其他各种用途的聚丙烯改性剂,尤其是需要延伸率和低温性能的应用,用作SEBS化合物的基聚合物,以及粘合剂和密封剂成分。例如,弹性带状薄膜、无涂层气囊盖、保险杠。 Asahi Kasei Tuftec™ H1062 is designed for an impact modifier of polypropylene (PP). It provides good balance of properties and can improve impact resistance property at room and low temperature. H1062 can be used as an additive to enhance heat sealability of PP film. Applications: Primarily as modifier of PP for automotive exteriors and interiors. Also effective as modifier of PP for other various applications, particularly those requiring elongation and low-temperature performance, as base polymer of SEBS compounds, and as adhesives and sealants component. E.g. elastic ribbon films, no-coat airbag covers, bumpers. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.890 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
4.5 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
67 | ISO 7619 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture 2 |
15.0 | MPa | ISO 37 |
300% 应变 300% strain |
4.30 | MPa | ISO 37 |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ISO 37 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Styrene/Rubber ratio Styrene/Rubber ratio |
内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1A, 20 in/min |
【新闻资讯】查看全部
加大废弃塑料及工业固废资源化利用力度
2022-03-10 2022年政府工作报告提出,加强固体废物和新污染物治理,推行垃圾分类和减量化、资源化。固体废物治理与再利用,成为代表委员们热议话题之一。全国政协委员,集团公司董事长、党 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |