牌号简介 About |
---|
CONATHANE® CE-1155是一种双组分溶剂型聚氨酯印制电路板涂料,设计用于恶劣环境。CONATHANE® CE-1155具有优异的防潮性和良好的耐磨性。固化膜坚硬,对酚醛和环氧玻璃层压板具有良好的粘合性。当在印刷电路图案上进行测试时,使用1.5 mil薄膜可获得良好的结果。有缺陷的部件可以在涂层区域使用普通的维修程序进行更换,而不会退化或变色。然后可以完成点重新涂层。CONATHANE® CE-1155可通过喷涂、浸渍或刷洗技术应用,并在室温或高温下固化。固化膜适用于高达130°C的连续操作。该系统含有荧光染料,以帮助在紫外线下进行检查。 CONATHANE CE-1155 is a two-component, solvent-based polyurethane printed circuit board coating designed for use in adverse environments. CONATHANE CE-1155 provides outstanding resistance to moisture and good abrasion resistance. The cured film is hard and tough and has excellent adhesion to phenolic and epoxy-glass laminates. When tested over printed circuit patterns, excellent results are obtained with 1.5 mil films. Defective components can be replaced in coated areas using ordinary repair procedures without degradation or discoloration. Spot re-coating can then be accomplished. CONATHANE CE-1155 may be applied by spray, dip, or brush techniques and will cure at room or elevated temperatures. The cured film is suitable for continuous operation up to 130°C. The system contains a fluorescent dye to aid inspection under ultraviolet light. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- 2 |
0.958 | g/cm³ | |
-- -- 3 |
1.13 | g/cm³ | |
固体含量 Solid content |
|||
Hardener Hardener |
64 到 66 | % | |
Resin Resin |
60 | % | |
粘度 viscosity |
Brookfield | ||
固化剂,25℃ Curing agent, 25 ℃ |
0.07 | Pa·s | Brookfield |
树脂,25℃ Resin, 25 ℃ |
Pa·s | Brookfield | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
铅笔硬度 Pencil hardness |
|||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ||
体积电阻率 Volume resistivity |
|||
25 ℃ 25 ℃ |
ohms·cm | ||
介电强度 Dielectric strength |
|||
0.0508 mm 0.0508 mm |
kV/mm | ||
0.559 mm 0.559 mm |
kV/mm | ||
介电常数 Dielectric constant |
|||
25 ℃,100 Hz 25 ℃,100 Hz |
|||
25 ℃,1 kHz 25 ℃,1 kHz |
|||
25 ℃,1 MHz 25 ℃,1 MHz |
|||
耗散因数 Dissipation factor |
|||
25℃,100 Hz 25℃,100 Hz |
|||
25℃,1 kHz 25℃,1 kHz |
|||
25℃,1 MHz 25℃,1 MHz |
|||
绝缘电阻 insulation resistance 4 |
|||
25℃ 25℃ 4 |
ohms | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
闪点 flash point |
|||
Hardener Hardener |
℃ | ||
Resin Resin |
℃ | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
储存稳定性 storage stability 5 |
|||
25 ℃ 25 ℃ 5 |
min | ||
贮藏期限 Storage period |
|||
25℃ 25℃ |
wk | ||
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
25℃ 25℃ |
cP | ASTM D2393 | |
脱模时间 stripping time |
|||
25℃ 25℃ |
min | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
抗真菌性 Antifungal activity |
ASTM G21 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Hardener |
3 Resin |
4 Initially and 50% R.H. |
5 400 Gram Mass |
【新闻资讯】查看全部
煤制烯烃新减产能集中投产 聚丙烯供应压力加大
2016-05-03 受原油上涨和资金推动的影响,聚丙烯期货自2015年12月底触底反弹。今年3月至今,由于前期的上涨没有得到基本面的配合,聚丙烯价格呈现高位宽幅振荡走势,振荡区间在6600―7100元/吨,聚丙烯振荡两个月说明目前多空双方的分歧比较大,市场正在寻找方向。笔者下文着重从基本面的角度来论述未来聚丙烯价格朝哪个方向突破的概率较大。 新增产能集中投产,供给压力显现 近几年是煤制烯烃装置投产的密集期,由于2015年烯烃价格暴跌,导致了部分煤制烯烃企业推迟投产计划,从而造成 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |