牌号简介 About |
---|
HD53-7000是经认证的一级产品,设计用于多腔薄壁食品容器的注塑成型。HD53-7000具有窄分子量分布,具有优良的加工性、良好的冲击强度、良好的尺寸稳定性和良好的抗翘曲性。HD53-7000建议的加工温度为210至230°C。模具温度为20至40°C。HD53-7000符合FDR法规21CFR 177.1520(c)3.1a和大多数有关使用聚乙烯与食品接触的国际法规。 HD53-7000 is a certified prime grade designed for injection molding of multi-cavity thin-wall food containers. HD53-7000 features a NARROW molecular weight distribution offering excellent processability, good impact strength, good dimensional stability and good warpage resistance. HD53-7000 recommended processing temperature is 210 to 230°C.with mold @ 20 to 40°C. HD53-7000 complies with FDR regulation 21CFR 177.1520(c) 3.1a and most international regulations concerning the use of Polyethylene in contact with food articles. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.953 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
70 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
屈服 yield 2 |
20.7 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
10 | % | ASTM D638 |
弯曲模量 Bending modulus |
|||
2% 正割 2% secant |
1030 | MPa | ASTM D790 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸冲击强度 Tensile impact strength |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
【新闻资讯】查看全部
匈牙利动力集团MOL正式启动多元醇项目
2017-08-01 匈牙利能源集团摩尔(MOL)已正式启动其多元醇项目。公司目前已获许生产环氧丙烷,环氧丙烷是生产聚醚的重要原料。 集团已于昨日,与赢创(Evonik)及蒂森克虏伯(Thyssenkrupp)签署相关协议,获得核心生产技术。 该项目是摩尔工业转型战略的重要一步。摩尔已投资16.5亿欧元,约合130亿人民币,计划将公司由单一石化产业转型发展成特种化学品企业,该次转型预计于2021年前完成。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |