牌号简介 About |
---|
MVR (300 °C/1.2 kg) 5.0 cm³/10 min; 20 % 玻纤增强;阻燃; UL 94V-0/1.5 mm 和 5VA/3.0 mm; 高粘度; 易脱模; 注塑成型- 熔体温度:310 - 330 °C; 挤出; 只有不透明颜色可选 MVR (300 °C/1.2 kg) 5.0 cm³/10 min; 20 % glass fiber reinforced; flame retardant; UL 94V-0/1.5 mm and 5VA/3.0 mm; high viscosity; easy release; injection molding - melt temperature 310 - 330 °C; extrusion; available in opaque colors only |
产品描述 Product Description
厂家:德国科思创 Covestro
类别:PC Polycarbonate
颜色:可用颜色,不透明
加工条件:挤出 Extrusion
性能特点: 防火阻燃等级V-0; 含脱模剂; 高粘度; 防火阻燃等级V-2; 阻燃; 防火阻燃等级5VA; High Viscosity,Good stripping performance,Flame Characteristics,V-2,V-0,5VA
填料:玻璃纤维 20
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.34 | g/cm³ | ISO 1183 |
表观密度 Apparent density 2 |
0.64 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
6.0 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
5.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD TD |
0.30 to 0.50 | % | ISO 2577 |
MD MD |
% | ISO 2577 | |
TD:2.0 mm TD:2.0 mm 3 |
% | ISO 294-4 | |
MD:2.0 mm MD:2.0 mm 3 |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 6 |
|||
23℃,完全断裂 23 ℃, completely fractured 6 |
kJ/m² | ISO 7391 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-60℃,完全断裂 -60 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
23℃,完全断裂 23 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 7 |
|||
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
ISO 6603-2 | ||
-30℃ -30℃ |
J | ISO 6603-2 | |
23℃ 23℃ |
J | ISO 6603-2 | |
多轴向仪器化冲击力峰值 Multi axial instrumented peak impact force |
ISO 6603-2 | ||
-30℃ -30℃ |
N | ISO 6603-2 | |
23℃ 23℃ |
N | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
136℃ 136℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient 8 |
|||
23℃ 23℃ 8 |
W/m/K | ISO 8302 | |
相对温度指数 电气性能 Relative temperature index electrical performance |
|||
1.50 mm 1.50 mm |
℃ | UL 746 | |
相对温度指数 机械冲击性能 Relative temperature index mechanical impact performance |
|||
相对温度指数 静态 Relative temperature index static |
|||
1.50 mm 1.50 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
解决方案 A Solution A |
V | IEC 60112 | |
解决方案 B Solution B |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.50 mm 0.50 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index 9 |
% | ISO 4589-2 | |
小型燃烧器火焰的应用 The Application of Small Burner Flames |
|||
2.00 mm 2.00 mm |
DIN 4102 | ||
Method K and F:2.00 mm Method K and F:2.00 mm |
DIN 53438-1, -3 | ||
燃烧速率 Burning rate |
|||
USFMVSS,> 1.00 mm USFMVSS,> 1.00 mm |
ISO 3795 | ||
闪点温度 Flash point temperature |
℃ | ASTM D1929 | |
针焰测试 Needle flame test |
IEC 60695-11-5 | ||
Method F:1.50 mm Method F:1.50 mm |
min | IEC 60695-11-5 | |
Method F:2.00 mm Method F:2.00 mm |
min | IEC 60695-11-5 | |
Method F:3.00 mm Method F:3.00 mm |
min | IEC 60695-11-5 | |
Method K:1.50 mm Method K:1.50 mm |
min | IEC 60695-11-5 | |
Method K:2.00 mm Method K:2.00 mm |
min | IEC 60695-11-5 | |
Method K:3.00 mm Method K:3.00 mm |
min | IEC 60695-11-5 | |
自燃温度 Autoignition temperature |
℃ | ASTM D1929 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
电解腐蚀 Electrolytic corrosion |
|||
23℃ 23℃ |
IEC 60426 | ||
ISO Shortname ISO Shortname |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
1 hr 1 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178 | |
弯曲应变 Bending strain 5 |
|||
23℃ 23℃ 5 |
% | ISO 178 | |
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Pellets |
3 60x60x2 mm, 500 bar |
4 0.079 in/min |
5 2 mm/min |
6 Based on ISO 179-1eA, 3 mm |
7 Based on ISO 180-A, 3 mm |
8 Cross-flow |
9 程序 A |
【新闻资讯】查看全部
EVA是什么资料?eva多少钱一个立方米
2019-07-23 乙烯-醋酸乙烯共聚物,简称EVA。一般醋酸乙烯(VA)的含量在5%-40%,与聚乙烯(PE)相比,EVA由于在分子链中引入醋酸乙烯单体,从而降低了高结晶度,提高了韧性、抗冲击性、填料相溶 |
EVA是什么资料?eva多少钱一个立方米
乙烯-醋酸乙烯共聚物,简称EVA。一般醋酸乙烯(VA)的含量在5%-40%,与聚乙烯(PE)相比,EVA由于在分子链中引入醋酸乙烯单体,从而降低了高结晶度,提高了韧性、抗冲击性、填料相溶性和热密封性能,被广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域。
EVA的应用领域:
1、广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域。
2、乙酸乙烯含量在5%~10%的EVA产品为弹性薄膜等;
3、乙酸乙烯含量在20~28%的EVA,主要用于热熔粘合剂和涂层制品;
4、乙酸乙烯含量在5%~45%,主要产品为薄膜(包括农用薄膜)和片材,注塑、模塑制品,发泡制品,热熔粘合剂等。
(1)发泡鞋材。鞋材是我国EVA树脂最主要的应用领域。在鞋材使用的EVA树脂中,醋酸乙烯含量一般在15%~22%。由于EVA树脂共混发泡制品具有柔软、弹性好、耐化学腐蚀等性能,因此被广泛应用于中高档旅游鞋、登山鞋、拖鞋、凉鞋的鞋底和内饰材料中。另外,这种材料还用于隔音板、体操垫和密封材领域。
(2)薄膜。EVA薄膜的主要用途是生产功能性棚膜。功能性棚膜具有较高的耐候、防雾滴和保温性能,由于聚乙烯不具有极性,即使添加一定量的防雾滴剂,其防雾滴性能也只能维持2个月左右;而添加一定量EVA树脂制成的棚膜,不仅具有较高的透光率,而且防雾滴性能也有较大提高,一般可超过4个月。另外,EVA还可用于生产包装膜、医用膜、层压膜、铸造膜等。
(3)电线电缆。随着计算机及网络工程的不断发展,出于对机房安全的考虑,人们越来越多地使用无卤阻燃电缆和硅烷交联电缆。由于EVA树脂具有良好的填料包容性和可交联性,因此在无卤阻燃电缆、半导体屏蔽电缆和二步法硅烷交联电缆中使用较多。另外,EVA树脂还被应用于制作一些特殊电缆的护套。在电线电缆中使用的EVA树脂,醋酸乙烯含量一般在12%~24%。
(4)玩具。EVA树脂在玩具中也有较多应用,如童车轮、座垫等。
(5)热熔胶。以EVA树脂为主要成分的热熔胶,由于不含溶剂,不污染环境且安全性较高,非常适合于自动化的流水线生产,因此被广泛应用于书籍无线装订、家具封边、汽车和家用电器的装配、制鞋、地毯涂层和金属的防腐涂层上。
(6)其他。EVA树脂在油墨、箱包、酒瓶垫盖等领域也有较为广泛的应用,估计这些方面消耗EVA树脂不少于15kt。
EVA材料它的应用非常广泛,在很多领域都可以看到它的身影。不知道大家是否知道发泡鞋鞋材是我国EVA树脂最主要的应用领域。由于EVA树脂共混发泡制品具有柔软、弹性好、耐化学腐蚀等性能,因此被广泛应用于中高档旅游鞋、登山鞋、拖鞋、凉鞋的鞋底和内饰材料中。它常用在cosplay时需要做道具,又或者是用来做模型。还有平时经常见到的电线电缆也是由于EVA树脂具有良好的填料包容性和可交联性,因此在无卤阻燃电缆、半导体屏蔽电缆和二步法硅烷交联电缆中使用较多。
EVA的价格:
不同厂家、不同牌号的价格会有所不同,各牌号具体价格详见搜料报价中心数据库
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。