| 牌号简介 About |
|---|
| Vibrathane 8083是一种TDI端接聚酯基预聚物，当用4,4’-亚甲基双（邻氯苯胺），通常称为MBCA固化时，可得到85邵尔A硬度的聚氨酯。这种预聚物在室温下是液态的，在加工温度下表现出低粘度，并且特别耐热。Vibrathane® 8083弹性体的特点是：高拉伸和撕裂强度。优异的耐热性、耐燃油性和耐溶剂性。优异的耐磨性。良好的低温和动态性能。 VIBRATHANE 8083 is a TDI-terminated polyester based prepolymer which yields an 85 Shore A hardness urethane when cured with 4,4'-methylene bis-(orthochloroaniline), commonly called MBCA. This prepolymer is liquid at room temperature, exhibits low viscosities at processing temperatures and is exceptionally heat stable. Vibrathane 8083 elastomers are characterized by: High tensile and tear strength. Excellent heat, fuel and solvent resistance. Outstanding abrasion resistance. Good low temperature and dynamic properties. |
产品描述 Product Description
性能特点： 拉伸性能好; 热稳定性好; 耐磨; 机械强度好-撕裂; 耐化学性; 耐高温; 低粘度; 耐燃油; Low Viscosity,High Heat Resistance,Good Tensile Strength,Good tear strength,Good wear resistance,Solvent resistance,Heat Stabilized,Fuel resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.25 | g/cm³ | ASTM D792 |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
100% 应变 100% strain |
5.03 | MPa | ASTM D412 |
|
300% 应变 300% strain |
8.73 | MPa | ASTM D412 |
|
拉伸强度 tensile strength |
42.7 | MPa | ASTM D412 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
660 | % | ASTM D412 |
|
撕裂强度 tear strength |
|||
|
-- -- 2 |
kN/m | ASTM D624 | |
|
开裂 cracking |
kN/m | ASTM D470 | |
|
压缩形变 Compression deformation |
|||
|
70℃，22 hr 70℃，22 hr |
% | ASTM D395B | |
|
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热固组件 Thermosetting components |
|||
|
树脂 resin |
|||
|
硬化法 Hardening method |
|||
|
储存稳定性 storage stability |
min | ||
|
后固化时间 Post curing time |
|||
|
100℃ 100℃ |
hr | ||
|
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
固化时间 Curing time |
|||
|
100℃ 100℃ |
hr | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A Shaw's A |
ASTM D2240 | ||
|
泰伯耐磨性 Taber abraser |
|||
|
5000 周期，1000 g，H-18 转轮 5000 cycles, 1000 g, H-18 wheels |
mg | ASTM D1044 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 C 模具 |
|
【新闻资讯】查看全部 
世界级光学膜产业基地花落新疆乌鲁木齐
2016-09-21 新疆凯沃新材料科技股份有限公司联合全球多家知名集团，在新疆乌鲁木齐高新区(新市区)北区科技创新园共同打造的“世界级光学膜产业基地”，已于9月19日开工建设。 新疆乌鲁木齐高新区(新市 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付