| 牌号简介 About |
|---|
| 符合ISO 1043-1的化学缩写：POM成型化合物ISO 9988-POM-K，M-GNR，02-003，GF26 POM共聚物注射成型型，用Ca 26%玻璃纤维增强；高耐热性和氧化降解性；减少热膨胀和收缩。所有颜色和厚度超过1.57 mm的UL注册为UL 94 HB，温度指数为UL 746 B，电气105°C，机械95°C（拉伸冲击）和100°C（拉伸）。燃烧速率ISO 3795和FMVSS 302<100 mm/min，厚度大于1 mm。适用范围：适用于高强度、高刚度、高硬度的成型件。fmvss=联邦机动车安全标准（美国）ul=保险商实验室（美国） Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GNR, 02-003, GF26 POM copolymer Injection molding type, reinforced with ca 26 % glass fibers; high resistance to thermal and oxidative degradation; reduced thermal expansion and shrinkage. UL-registration for all colours and a thickness more than 1.57 mm as UL 94 HB, temperature index UL 746 B electrical 105 °C, mechanical 95 °C (tensile impact) and 100 °C (tensile). Burning rate ISO 3795 and FMVSS 302 < 100 mm/min and a thickness more than 1 mm thickness. Ranges of applications: For molded parts with very high strength and rigidity as well as higher hardness. FMVSS = Federal Motor Vehicle Safety Standard (USA) UL = Underwriters Laboratories (USA) |
产品描述 Product Description
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 机械强度好; 硬度高; Good Rigidity,Good Hardness,HB
填料：玻璃纤维 26
| 技术参数 Technical Data | |||
|---|---|---|---|
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
9200 | MPa | ISO 527-2/1A/1 |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
135 | MPa | ISO 527-2/1A/5 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
2.5 | % | ISO 527-2/1A/5 |
|
Tensile Creep Modulus（1 hr） Tensile Creep Modulus（1 hr） |
7700 | MPa | ISO 899-1 |
|
拉伸蠕变模量 Tensile creep modulus |
|||
|
1000 hr 1000 hr |
5400 | MPa | ISO 899-1 |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
8.0 MPa，未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
1/℃ | ISO 11359-2 | |
|
MD MD |
1/℃ | ISO 11359-2 | |
|
Effective Thermal Diffusivity Effective Thermal Diffusivity |
cSt | Internal Method | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
相对电容率 Relative permittivity |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
1.60 mm 1.60 mm |
UL 94 | ||
|
3.20 mm 3.20 mm |
UL 94 | ||
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
g/cm³ | ISO 1183 | |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
190℃，2.16 kg 190℃，2.16 kg |
cm³/10min | ISO 1133 | |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
Density of Melt Density of Melt |
g/cm³ | Internal Method | |
|
Specific Heat Capacity of Melt Specific Heat Capacity of Melt |
J/kg/℃ | Internal Method | |
|
Thermal Conductivity of Melt Thermal Conductivity of Melt |
W/m/K | Internal Method | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 10°C/min |
|
【新闻资讯】查看全部 
龙佰集团与比克电池签署战略合作框架协议
2021-12-12 搜料网资讯： 龙佰集团发布公告，近日，公司与深圳市比克电池有限公司(简称比克电池)签署了《战略合作框架协议》，双方建立战略合作伙伴关系。双方立足于以长远高质量发展为目 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付