牌号简介 About |
---|
Xenoy CL100S是专门开发的,以获得良好的低温冲击强度,优异的紫外线稳定性和耐偶然溶剂和汽油接触。Xenoy CL100S特别适用于未喷漆的外部汽车车身部件。 XENOY CL100S has been specifically developed to obtain good low temperature impact strength, excellent UV stability and resistance to occasional solvent and gasoline contact. XENOY CL100S is particularly suited for unpainted exterior automotive body components. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PC+PBT PC+PBT
用途:汽车外部零件;
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级HB; 耐汽油; 耐化学性; 耐低温冲击; 耐候抗UV; Weather resistance is good,Solvent resistance,low-temperature impact resistance,Gasoline resistance,HB
紫外线:UV Stabilized
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.22 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
250℃,5 kg 250℃,5 kg |
20.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate 3 |
内部方法 | ||
MD MD |
0.70 到 1.0 | % | 内部方法 |
TD TD |
0.70 到 1.0 | % | 内部方法 |
吸水率 Water absorption rate |
ISO 62 | ||
饱和,23℃ Saturation, 23 ℃ |
0.50 | % | ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ 6 |
kJ/m² | ISO 179/1eA | |
-30℃ -30℃ |
kJ/m² | ISO 179/2C | |
-20℃ -20℃ |
kJ/m² | ISO 179/2C | |
23℃ 23℃ 6 |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/2C | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 6 |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 7 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 7 |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 8 |
|||
0.45 MPa,未退火,100 mm跨距 0.45 MPa, unannealed, 100 mm span |
℃ | ISO 75-2/Be | |
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span |
℃ | ISO 75-2/Ae | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
75℃ 75℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
ISO 11359-2 | ||
MD:23~80℃ MD:23~80℃ |
1/℃ | ISO 11359-2 | |
TD:23~80℃ TD:23~80℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ISO 8302 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
IEC 60243-1 | ||
1 mm 1 mm 9 |
kV/mm | IEC 60243-1 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
60 Hz 60 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
60 Hz 60 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
燃烧速率 Burning rate |
|||
1 mm 1 mm |
mm/min | ISO 3795 | |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
L 级 Level L |
ISO 2039-2 | ||
球压硬度 Ball hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
ISO 527-2/50 | ||
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 4 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 , 5 |
MPa | ISO 178 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Tensile Bar |
3 0,079 in/min |
4 Yield |
5 80*10*4 sp=62mm |
6 80*10*4 |
7 120*10*4 mm |
8 Short-Time |
【新闻资讯】查看全部
普立万宣布收购 Fiber-Line公司
2019-01-04 2019年1月2日,全球领先的专业聚合物材料、服务和解决方案供应商 普立万 公司宣布以1.2亿美元收购全球定制工程纤维和复合材料领导者FiberLine公司。 Fiber-Line成立于1987年,利用其以客 |
普立万宣布收购 Fiber-Line公司 2019年1月2日,全球领先的专业聚合物材料、服务和解决方案供应商普立万公司宣布以1.2亿美元收购全球定制工程纤维和复合材料领导者FiberLine公司。普立万公司董事长、总裁兼首席执行官Robert M.Patterson说:“Fiber-Line是我们的光纤和复合解决方案业务中的一个创新和独特的补充,具有巨大的增长优势。它们在光纤电缆和未来5G网络的建设占据了直接的领导地位。” Patterson先生补充道:“此次收购是我们特殊工程材料部门的重大投资。我们预计,该公司在2019年将增加近1亿美元的收入,并立即增加每股收益。” Fiber-Line的领先技术补充了普立万现有的专业复合解决方案和电线电缆应用。普立万将利用其成熟的投资增长整合战略,通过利用更深层次的配方专业知识和加速增长的全球商业存在,为光纤线客户提供创新方案。 “加入普立万团队代表着Fiber-Line员工和我们尊贵客户的另一个重要和激动人心的里程碑,”Fiber-Line首席执行官DaleOuthous说。“通过普立万对Fiber-Line技术能力、运营和商业范围的未来投资,我们将能够比以往更好地为客户服务。” Patterson先生补充道:“我们非常高兴欢迎Dale和他那有成就的Fiber-Line管理团队来到普立万。通过加强与客户的合作,我们将抓住近期增长前景,并从5G网络的扩展中获益。从长远来看,我们预计未来的增长将由纤维和复合材料之间的显著技术协同作用推动,利用普立万公司很擅长开发的特殊着色剂和涂层我们将达到这一目标。” |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
原厂数据及认证:
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。