| 牌号简介 About |
|---|
| 缩醛共聚物级JPAC是一种中等粘度的聚合物，在一般用途的薄壁管和薄膜的注射成型和挤出中提供最佳性能。 Acetal copolymer grade JPAC is a medium viscosity polymer providing optimum performance in general purpose injection molding and extrusion of thin walled tubing and thin gauge film. |
产品描述 Product Description
用途：轴承;阀门/阀门部件;泵件;齿轮;弹簧;外壳;凸轮;旋钮;
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 尺寸稳定性好; 共聚物; 表面光泽度好; 韧性好; 易加工; Excellent Processability,Good flexibility,Good surface appearance,Good Dimensional Stability,Copolymer,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.41 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
9.0 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
ASTM D955 | ||
|
MD MD |
2.2 | % | ASTM D955 |
|
TD TD |
1.8 | % | ASTM D955 |
|
吸水率 Water absorption rate |
ASTM D570 | ||
|
24hr 24hr |
0.22 | % | ASTM D570 |
|
饱和 saturated |
% | ASTM D570 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ASTM D570 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
J/m | ASTM D256 | |
|
拉伸冲击强度 Tensile impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ASTM D1822 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ASTM D648 | ||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
玻璃化转变温度 Glass transition temperature |
℃ | ASTM E1356 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
熔融温度 Melting temperature |
℃ | ||
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1/℃ | ASTM D696 | |
|
比热 specific heat |
J/kg/℃ | ASTM C351 | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
|
相对温度指数 Relative temperature index |
UL 746 | ||
|
电气性能 Electrical performance |
UL 746 | ||
|
1.5 mm 1.5 mm |
℃ | UL 746 | |
|
3.0 mm 3.0 mm |
℃ | UL 746 | |
|
6.1 mm 6.1 mm |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
UL 746 | ||
|
1.5 mm 1.5 mm |
℃ | UL 746 | |
|
3.0 mm 3.0 mm |
℃ | UL 746 | |
|
6.1 mm 6.1 mm |
℃ | UL 746 | |
|
1.50 mm 1.50 mm |
℃ | UL 746 | |
|
3.00 mm 3.00 mm |
℃ | UL 746 | |
|
6.10 mm 6.10 mm |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
100 Hz 100 Hz |
ASTM D150 | ||
|
10 kHz 10 kHz |
ASTM D150 | ||
|
1.00 GHz 1.00 GHz |
ASTM D150 | ||
|
1.02 mm，1 kHz 1.02 mm，1 kHz |
ASTM D150 | ||
|
1.02 mm，1 MHz 1.02 mm，1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
100 Hz 100 Hz |
ASTM D150 | ||
|
10 kHz 10 kHz |
ASTM D150 | ||
|
1.02 mm，1 kHz 1.02 mm，1 kHz |
ASTM D150 | ||
|
1.02 mm，1 MHz 1.02 mm，1 MHz |
ASTM D150 | ||
|
耐电弧性 Arc resistance |
sec | ASTM D495 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
|||
|
屈服，23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
|||
|
断裂 fracture |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
剪切强度 shear strength |
|||
|
23℃ 23℃ |
MPa | ASTM D732 | |
|
摩擦系数 friction coefficient |
ASTM D1894 | ||
|
与金属 - 静态 Metal - Static |
ASTM D1894 | ||
|
与自身 - 静态 With oneself - static |
ASTM D1894 | ||
|
泰伯耐磨性 Taber abraser |
ASTM D1044 | ||
|
1000 周期，CS-17 转轮 1000 cycles, CS-17 wheel |
mg | ASTM D1044 | |
|
1000 周期，CS-17F 转轮 1000 cycles, CS-17F wheel |
mg | ASTM D1044 | |
|
1000 周期，CS-18 转轮 1000 cycles, CS-18 wheel |
mg | ASTM D1044 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
塑料摩擦系数ASTM D1894
2017-07-03 塑料摩擦系数ASTM D1894 范围： 该测试用于确定被拖动到另一个表面的动力学(移动)和静态(起始)电阻。 试验程序： 试样附在规定重量的滑雪板上。雪橇以150毫米/分钟的速度穿过第二个表 |
|