牌号简介 About |
---|
TOPAS® 8007S-04是一种环烯烃共聚物 (COC)产品。特别为医疗保健和药品包装而制造的,具有高防潮性能的特殊成型等级 TOPAS® 8007S-04 Product Description TOPAS 8007S-04 is a general purpose injection molding grade. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for healthcare and other high-tech products. Lower leachables and extractables of TOPAS COC preserve content stability and quality. It is a non-polar substrate that does not promote adsorption, denaturation, aggregation, or precipitation like glass can. Analytical results are more accurate with TOPAS COC in contact with sensitive chemistries. Selected Applications Drug delivery Prefilled syringes, vials, cartridges Bottles and tubes Surgical instruments IV containers and components Labware Optics Electronics Food packaging Healthcare and food contact Leading Attributes Low leachables & extractables, low water transmission Non-ionic, does not promote adsorption like glass Minimally reactive Chemically resistant to alcohol, acetone, and acrylates Transparent, withstands EtO and gamma sterilization Temperature resistance, clarity and purity Clarity, low birefringence, low moisture sensitivity Low dielectric constant, thermoplastic Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Injection Molding, Healthcare, Optics and Diagnostics TOPAS 8007X10 - our highest ultraviolet (UV) transmission grade TOPAS® 8007S-04 TOPAS® 8007S-04 is a Cyclic Olefin Copolymer (COC) product. It is available in Africa & Middle East, Asia Pacific, or Latin America. Characteristics include: Flame Rated Copolymer |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.01 | g/cm³ | ISO 1183 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.01 | % | ISO 62 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,2.16kg 260℃,2.16kg |
32 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
23℃ 23℃ |
63 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
4.5 | % | ISO 527-2 |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
|||
2000 μm 2000 μm |
% | ISO 13468-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357-2 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻 Volumetric resistance |
Ω.cm | IEC 60093 | |
介电常数 Dielectric constant |
|||
23℃ 23℃ |
1 kHz | IEC 60250 | |
耗散因数 Dissipation factor |
|||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50mm 1.50mm |
UL-94 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Dependent on processing conditions and part design. |
3 10°C/min |
【新闻资讯】查看全部
美国塑料行业就业人数上升,全行业预期出现增长趋向
2018-01-10 美国塑料工业协会(Plastics Industry Association)的最新数据分析显示美国塑料市场前景乐观。 这家总部位于华盛顿的贸易协会于12月中旬发布了2017年规模及影响报告。该集团还举办了一场关于该报告的网络研讨会,由公司总裁兼首席执行官比尔-卡特奥克斯及首席经济学家佩克-皮内达主持。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |