牌号简介 About |
---|
FRblend® PC-1309是15%玻璃纤维增强,阻燃聚碳酸酯化合物。阻燃体系是基于溴化阻燃剂。该牌号具有优异的抗冲击性、良好的尺寸稳定性、高耐热性和良好的表面性能。 FRblend® PC-1309 is 15% glass fiber reinforced, flame retardant polycarbonate compound. The flame retardant system is based on brominated flam retardant. This grade offers excellent impact resistance, good dimensional stability, high heat resistance and good surface. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.32 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
10 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.30 到 0.50 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.12 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
7360 | MPa | ASTM D638 |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
全球调查:四分之三调查对象希望尽快禁用一次性塑料制品
2022-02-24 民意调查机构益普索集团2月22日发布的一项全球调查显示,四分之三调查对象希望全球范围内尽快禁用一次性塑料制品。2019年同类调查中这一比例为71%。 图为2019年5月28日,在马来西亚 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |