牌号简介 About |
---|
Styrolution PS 158K是耐热、速冻通用等级。它适用于发泡片材和薄膜;用于在热接触应用中具有高冲击聚苯乙烯(PS)的共混物;用于与苯乙烯(Styrolux)共混物的透明耐冲击应用。高耐热GPPS高透明度应用取代SAN在几个应用,如水过滤器容器,笔部件等。用于展示和显示的透明片,消费电子,家用,相框,建筑材料等。物理或化学发泡的高质量泡沫的理想材料与高抗冲聚苯乙烯或苯乙烯基注塑制品共混的泡沫容器、标签或型材(PSP/XPS)等制品 Styrolution PS 158K is a heat resistant, rapid freezing general purpose grade. It is suitable for expanded sheet and film; for blends with high impact Styrolution PS in heat contact applications; for transparent, impact resistant applications in blends with Styrolux. FEATURES High heat resistance GPPS High transparency APPLICATIONS Replacement of SAN in several application like water filter containers, pen parts etc. Transparent sheet for Showcases & displays, consumer electronics, household application, photo frames, building material etc. Ideal material for physically or chemically foamed high-quality foamed articles, such as foam containers, labels or profiles (PSP/XPS) In blends with high impact polystyrene or Styrolux Injection molded articles |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 | g/cm³ | ISO 1183 |
表观密度 Apparent density 3 |
0.60 | g/cm³ | |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
3.0 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
200℃,5 kg 200℃,5 kg |
3.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage |
0.30 到 0.60 | % | ISO 294-4 |
吸水率 Water Absorption |
ISO 62 | ||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT 4 |
|||
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temperature |
|||
-- -- |
℃ | ASTM D1525 5 | |
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Coeff.of linear therm expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
导热系数 Thermal Conductivity |
W/m/K | DIN 52612 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength 6 |
|||
1.5 mm 1.5 mm 6 |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
球压硬度 ball-indentation hardness |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
拉伸蠕变模量 Tensile creep modulus |
ISO 899-1 | ||
1 hr 1 hr |
MPa | ISO 899-1 | |
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲强度 Flexural Strength |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 With external lubricant |
3 4h/80°C |
4 标准 B (120°C/h), 压 力1 (10N) |
5 Short Time |
【新闻资讯】查看全部
ABS的注塑加工工艺
2018-09-26 ABS塑料由于具有较大的机械强度和良好的综合性能,在电子工业、机械工业、交通运输、建筑材料、玩具制造等工业中占有重要的位置,特别是稍微大型的箱体结构以及受力元件,需要电镀的装饰件更是离不开这种塑料。笔者根据多年的实践经验,对ABS塑料注塑工艺作如下分析。 (1)ABS塑料的干燥ABS塑料的吸湿性和对水分的敏感性较大,在加工前进行充分的干燥和预热,不但能消除水汽造成的制件表面烟花状泡带、银丝,而且还有助于塑料的塑化,减少制件表面色斑和云纹。ABS原料要控制水分在013%以下。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |