牌号简介 About |
---|
Metton-LMR反应注射成型工艺可以在低压模具中提供与注塑工程热塑性塑料类似的力学性能的大型零件。Metton LMR的工艺和材料能力的结合,为取代金属、木材和玻璃纤维等传统材料带来了新的设计自由。纤维增强制品的耐久性较差,但等效截面模量较高。在大多数半结构应用中,Metton LMR的设计可为性能提供等效的部件刚度,并且通常能够显著减轻重量。本节包含最初评估Metton LMR与特定应用的兼容性所需的聚合物性能数据。Metton LMR产品系列包括标准M15xx产品系列和满足U.L.V-O分类要求的阻燃产品。Metton M15xx包括M1534、M1537、M1539和M1540产品。梅顿V-0产品采用了一种特殊的三流轮辋注射机。 The Metton LMR reaction injection molding process can provide large parts in low pressure molds with the mechanical property performance similar to injection molded engineering thermoplastics. The combination of Metton LMR's process and material capabilities result in a new design freedom for replacing traditional materials such as metal, wood and fiberglass. Fiber reinforced products tend to have poorer durability, but higher equivalent section modulus. In most semi-structural applications, Metton LMR can be designed to provide equivalent part stiffness for performance and generally at a significant weight reduction. This section contains polymer property data necessary to initially assess the compatibility of Metton LMR with a particular application. The Metton LMR product family includes a standard M15XX product line and a flame-retardant product which meets the requirements for classification as U.L. V-O. The Metton M15XX includes the products M1534, M1537, M1539 and M1540. The Metton V-0 product uses a special three stream RIM injection machine. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.03 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.90 | % | |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.12 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃ -40℃ |
110 | J/m | ASTM D256 |
23℃ 23℃ |
460 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature |
℃ | DMA | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:0~50℃ MD:0~50℃ |
1/℃ | ASTM D696 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
5% 应变 5% strain |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
泊松比 Poisson's ratio |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
廉价航空巨头来了!美国第五大航空公司也呼之欲出
2022-02-08 美国最大的两家廉价航空公司边疆航空(Frontier Airlines)和精神航空公司(Spirit Airlines)已同意合并,合并后将成为美国第五大航空公司。 根据合并协议,该交易估值为66亿美元,包括承担净 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |