牌号简介 About |
---|
Lumicene MPE M5510 EP是第二代茂金属高密度均聚聚乙烯。与传统的LLDPE和第一代茂金属聚乙烯相比,鲁米新MPE M5510 EP的挤出压力低、气泡稳定性好、表观控制能力强,产量高。突出的刚度和良好的光学性能带来了显著的下降测量潜力。与常用的高密度聚乙烯相比,Lumicene MPE M5510 EP的高密度使其能够用于有防潮要求的应用中,如干食品包装,并带来了更好的耐热性。Lumicene MPE M5510 EP适用于包装袋、重型包装袋、自动包装专用薄膜、邮寄薄膜和层压等消费、工业、食品或卫生包装领域的许多应用。 Lumicene® mPE M5510 EP is a second generation metallocene high density homopolymer Polyethylene. Lumicene® mPE M5510 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The outstanding stiffness combined with good optical properties brings a significant down-gauging potential. The high density of Lumicene® mPE M5510 EP enables its use in applications with moisture barrier requirements, such as dry food packaging, and brings improved heat resistance, compared to commonly used HDPE. Lumicene® mPE M5510 EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as bags, heavy-duty sacks, automatic packaging specialty film, mailing film and lamination. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.955 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.2 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
40 | µm | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,40 µm,吹塑薄膜 MD, yield, 40 µ m, blow molded film |
27.5 | MPa | ISO 527-3 |
TD,屈服,40 µm,吹塑薄膜 TD, yield, 40 µ m, blow molded film |
28.0 | MPa | ISO 527-3 |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
MD:40 µm,吹塑薄膜 MD: 40 µ m, blow molded film |
N | ISO 6383-2 | |
TD:40 µm,吹塑薄膜 TD: 40 µ m, blow molded film |
N | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,40.0 µm,吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
2018,全球化工“超级周期”会来吗?
2018-01-12 IHS Markit近日表示,受消费升温和工业生产强劲增长推动,预计2018年全球化学品需求将趋旺,而且全球范围内各地区化学品产量也将同步增长。全球化工行业有望呈现稳中有升态势。该机构预计,2018年全球GDP增长率为3.2%,与2017年的增长率相当,高于2016年的2.5%。 产量增长亮眼 美国化工理事会(ACC)首席经济学家凯温・斯威夫特(Kevin Swift)表示,2018年全球化学品产量预计将增长3.2%,高于去年2.7%的增速。亚太、非洲发展中 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-TOTAL Polyethylene Lumicene® M 5510 EP证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)