牌号简介 About |
---|
聚碳酸酯,30%玻璃填充,阻燃 Polycarbonate, 30% Glass Filled, Flame Retardant |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.43 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
10 | g/10min | ASTM D1238 |
收缩率 Shrinkage |
|||
MD:3.2 mm MD:3.2 mm |
0.20 到 0.50 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
120 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
4.0 | % | ISO 527-2 |
弯曲模量 Flexural Modulus |
MPa | ISO 178 | |
弯曲强度 Flexural Strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部 ![]()
乙烯三聚制1-己烯新型催化零碎年省近4亿原料本钱
2016-02-03 近三年的时间里就为国内1-己烯用户节省近4亿元的原料成本,还使国际市场1-己烯产品价格下降了约三成。这就是荣获2015年国家技术发明二等奖的乙烯三聚制1-己烯新型催化体系及成套工艺技术。 乙烯三聚制1-己烯新型催化系统年省近4亿原料成本 用项目完成单位中国石化燕山石化科技部工作人员的话说就是:“燕山石化历时10年的不懈努力,打破了国外厂商对1-己烯的高 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |