牌号简介 About |
---|
Kingfa JH830T是一种聚碳酸脂合金(PC 合金)材料,。 该产品在北美洲或亚太地区有供货,加工方式为:注射成型。 Kingfa JH830T的主要特性有: 阻燃/额定火焰 高刚度 美观 典型应用领域包括: 电气用具 电线电缆 家庭应用 Kingfa JH830T is a Polycarbonate (PC) material. It is available in Asia Pacific or North America for injection molding. Important attributes of Kingfa JH830T are: Flame Rated Flame Retardant Good Processability Halogen Free Typical applications include: Electrical/Electronic Applications Appliances Business/Office Goods Household Applications Lighting Applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 | % | ASTM D995 |
TD TD |
0.70 | % | ASTM D995 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.12 | % | ASTM D570 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
132 | ℃ | ASTM D648 |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻 Volumetric resistance |
Ω.cm | ASTM D257 | |
表面电阻 Surface resistance |
Ω.cm | ASTM D257 | |
绝缘强度 Insulation strength |
|||
1.60mm 1.60mm |
KV/mm | ASTM D149 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
|
V-0 | UL 94 | |
|
V-0 | UL 94 | |
|
V-0 | UL 94 | |
|
V-0 | UL 94 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1 mm 1 mm |
℃ | IEC 60695-2-12 | |
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
灼热丝相对温度 Relative temperature of heating wire |
|||
0.75mm 0.75mm |
℃ | IEC 60695-2-13 | |
1.00mm 1.00mm |
℃ | IEC 60695-2-13 | |
1.60mm 1.60mm |
℃ | IEC 60695-2-13 | |
1.60mm 1.60mm |
℃ | IEC 60695-2-13 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
R 级 | ASTM D785 | |
拉伸强度 tensile strength |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D256 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.079 in/min |
【新闻资讯】查看全部
工业企业利润结构改善 下游行业成本压力缓解
2021-12-28 搜料网资讯: 随着保供稳价、助企纾困政策效果持续显现,11月工业企业利润结构有所改善,上游部分原材料价格快速上涨势头初步得到遏制,下游行业成本压力有所缓解。 国家统计局 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |