Menzolit® BMC 1500是一种基于不饱和聚酯树脂的整体模塑料。该产品是玻璃纤维增强,含有矿物填料。如果发生火灾,产品不会熔化,也不会形成液滴,也不会产生过量的烟雾。这种材料是在加热的钢模中注射成型的。建议使用镀铬工具。该产品不含卤素。Menzolit® BMC 1500是一种在高温下使用的特殊BMC。将玻璃含量设置为流动性好、强度和刚度性能好的水平。即使没有特定的阻燃剂,也能达到UL 94规定的阻燃HB。典型的应用是功能部件、家用和家电行业中的厨具外壳和盖子、铁把手和类似设备。 Menzolit® BMC 1500 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® BMC 1500 is a special BMC for the use at elevated temperature. The glass content is set to a level that combines good flowability with good strength and stiffness properties. Even without a specific fire retardant the fire retardancy HB according to UL 94 is achieved. Typical applications are functional components, housings and covers for kitchen ware, iron handels and similar equipment within the household and appliances industry. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.00 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
-- -- 2 |
0.0 | % | DIN 53464 |
-- -- |
0.30 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
< 0.50 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
模压成型 Compression Molding |
14000 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
模压成型 Compression Molding |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
连续使用温度 Continuous use temperature |
℃ | 内部方法 | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Glow Bar Glow Bar |
IEC 60707-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Post Molding Shrinkage |
【新闻资讯】查看全部
丙烯腈行业深陷亏损泥沼
2020-09-16 搜料网资讯: 自3月份开始,丙烯腈行业便身陷亏损泥沼,4月13日亏损额度一度扩大至3927.5元(吨价,下同),整个上半年理论平均盈亏在-859元,较去年同期下跌3650元左右,目前亏损额度 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |