牌号简介 About |
---|
Plexiglas® VH是一种热塑性丙烯酸树脂,用于注塑成型。它的特点是具有很高的熔体流动性。Plexiglas® VH具有优异的耐候性和光学性能,使其能够在要求室外稳定性、高质量表面外观和/或精密光学的应用中脱颖而出。Plexiglas® VH因其优异的热稳定性、挤出熔融强度和良好的工具表面再现和释放性能而易于加工。补充的Moldflow模拟数据可用。它对无机酸、碱和脂肪族碳氢化合物(如vm&p石脑油和庚烷)的溶液具有优异的抗药性。此外,它几乎不受各种商业产品的影响,包括许多饮料、食品、清洁剂溶液和清洁剂。 Plexiglas® VH is a thermoplastic acrylic resin formulated for injection molding applications. It is characterized by its very high melt flow. Plexiglas® VH has excellent weatherability and optical properties allowing it to excel in applications requiring outdoor stability, high quality surface appearance and/or precision optics. Plexiglas® VH is easy to process due to its exceptional thermal stability, extrusion melt strength, and excellent tool surface reproduction and release properties. Supplemental moldflow simulation data is available. It has excellent resistance to many chemicals including solutions of inorganic acids, alkalis and aliphatic hydrocarbons such as VM&P naphtha and heptane. Additionally, it is virtually unaffected by a wide range of commercial products including many beverages, foodstuffs, detergent solutions and cleaners. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.18 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,3.80kg 230℃,3.80kg |
20 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.20 to 0.60 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.30 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
16 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 2 |
|||
1.8 MPa,退火 1.8 MPa, annealed 2 |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed 2 |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 3 | |
-- -- |
℃ | ASTM D1525 4 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index 5 |
ASTM D542 | ||
透光率 Transmittance |
|||
3180 µm 3180 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
3180 µm 3180 µm |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ASTM Classification ASTM Classification |
ASTM D788 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Annealing cycle: 4hrs @ 70°F |
3 速率 A (50°C/h), 压 力1 (10N) |
4 速率 A (50°C/h), 载荷2 (50N) |
5 ND @ 72°F |
【新闻资讯】查看全部
靠科技创新降财务本钱
2016-02-03 新年伊始,围绕推进供给侧结构性改革这条主线,实现去杠杆、降成本已成为石油和化工行业推动经济持续健康发展的重要内容。如何摆脱产能过剩带来的困境,降低企业的财务风险,提升资本利用效率,降低负债率,改善市场供应结构?对此,笔者认为科技创新将唱主角。 科技创新可以有效去杠杆。当前,因项目建设缺乏全局性统筹谋划,不少化工产品遭遇产能过剩困扰,市场价格不断下滑,利润空间也不断收窄,导致化企财务成本居高不下。如何利用科技创新淘汰过剩产能,盘活存量资本,减轻杠杆压力,提高资源创效能力,将成 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |