| 牌号简介 About |
|---|
| 注射成型用PBT/ASA，化学增强30%玻璃纤维。在负温度下也具有优异的性能，如拉伸和弯曲的弹性模量、拉伸强度和韧性。不吸水，这意味着在潮湿环境中也能保持相同的性能。熔体具有很好的流变性，能够制造出具有复杂下流路径的极多种产品。与PA相比，缩孔的各向异性要好得多，这对圆孔、圆柱孔或其它孔产品的制造有很大的影响。在汽车、电气和工程行业中的应用-以自然模式和全RAL色标交付的电缆线束、汽车门锁、连接链节、把手等的连接器。 PBT/ASA for injection moulding, chemically reinforced with 30% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bending, tensial strength, toughness. Does not absorb water, that means that identical properties are maintained also in wet environment. Melt is characterised by very good rheology, which enables manufacturing of extremely multiple products with complicated downflow-path. Anisotropy of shrinkage is much better in comparison with PA, what influences the manufacturing of round, cylindric or other hole products. Application in the automotive, electrical and engineering industry - connectors of cable harnesses, car-door locks, connection links, grips etc. Delivered in natural mode and in the full RAL colour scale. |
产品描述 Product Description
用途：柔软的把手;工程配件;电气/电子应用领域;汽车领域的应用;连接器;
颜色：自然色,可用颜色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 化学耦合; 吸水率低; 耐低温韧性; Low or no water absorption,Chemical coupling,Low temperature toughness,HB
填料：玻璃纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.48 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
250℃，2.16kg 250℃，2.16kg |
10 | g/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
STM 64 0808 | ||
|
TD TD |
1.1 | % | |
|
MD MD |
0.91 | % | |
|
含水量 water content |
0.050 | % | ISO 960 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
|
-20℃ -20℃ |
kJ/m² | ||
|
23℃ 23℃ |
kJ/m² | ||
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
|
-20℃ -20℃ |
kJ/m² | ||
|
23℃ 23℃ |
kJ/m² | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 3146 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
美国CRTC用回收碳纤维加强树脂复合资料制造公园长椅
2017-05-16 位于华盛顿特区的复合材料回收技术中心 Composite Recycling Technology Center (CRTC)已收到城市公园和相关部门一万美元的种子资金，用于创建可回收的纤碳纤维增强树脂复合材料CFRP的公园长椅，作为试点项目。根据CRTC的首席执行官鲍勃・拉森(Bob Larsen)预计，这笔钱将抵消原型设计的成本和部分开发成本。 正如拉森所解释的那样，二十年来，这个城市一直在使用的长凳是用经过处理的木材和钢材制成的，这两种常规的材料由于存在盐水而腐蚀和生 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付