牌号简介 About |
---|
采用Unipol II工艺技术生产CONTINUUM™ DGDA-2490 BK GL双峰聚乙烯树脂。该产品可用于需要长期流体静强度和优异的抗缓慢裂纹扩展和快速裂纹扩展能力的管道应用。合适的应用包括天然气分配管道、工业管道、采矿、污水和市政供水管道。符合工业标准:ISO标准MRS 10/20°C,Exova CRS 10列出的PE100(20°C,100年);CRS 8(40°C,90年);CRS 6.3(60°C,11年);CRS 11.2(14°C,50年) CONTINUUM™ DGDA-2490 BK GL Bimodal Polyethylene Resin is produced using UNIPOL™ II process technology. This product may be utilized for pipe applications where long-term hydrostatic strength combined with outstanding resistance to slow crack growth and rapid crack propagation is desired. Suitable applications include natural gas distribution pipes, industrial piping, mining, sewage, and municipal water service lines. Industrial Standards Compliance: ISO Standard MRS 10 / 20°C, PE100 listed by Exova CRS 10 (20°C, 100 yr); CRS 8 (40°C, 90 yr); CRS 6.3 (60°C, 11 yr); CRS 11.2 (14°C, 50 yr) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
- - |
ISO 1183 | ||
黑色 black |
0.959 | g/cm³ | ISO 1183 |
|
0.949 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.080 | g/10min | ISO 1133 |
190℃,21.6kg 190℃,21.6kg |
7.5 | g/10min | ISO 1133 |
190℃,5.0kg 190℃,5.0kg |
0.31 | g/10min | ISO 1133 |
炭黑含量 Carbon black content |
% | ISO 6964 | |
Carbon Black Dispersion Carbon Black Dispersion |
ISO 18553 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 6259 | |
抗快速裂缝扩展,Pc - S-4(0℃) Resistance to rapid crack propagation, Pc-S-4 (0 ℃) |
bar | ISO 13477 | |
抗快速裂缝扩展,Tc - S-4 at 10 bar Anti rapid crack propagation, Tc-S-4 at 10 bar |
℃ | ISO 13477 | |
切口管材慢速裂纹增长 Slow crack growth in cut pipe materials 2 |
|||
80℃ 80℃ 2 |
hr | ISO 13479 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 6259 | |
for Buttfusion for Buttfusion |
ISO 13953 | ||
裂纹缓慢扩展 PENT Slow crack propagation PENT |
|||
348 psi,2.4 MPa,80℃ 348 psi,2.4 MPa,80℃ |
hr | ISO 16241 | |
流体静力学强度 Hydrostatic strength |
ISO 1167 | ||
1798 psi(12.4 MPa):20℃ 1798 psi(12.4 MPa):20℃ |
hr | ISO 1167 | |
783 psi(5.4 MPa):80℃ 783 psi(5.4 MPa):80℃ |
hr | ISO 1167 | |
798 psi(5.0 MPa):80℃ 798 psi(5.0 MPa):80℃ |
hr | ISO 1167 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
氧感应时间 Oxygen sensing time |
min | ISO 11357-6 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 133 psi (0.92 MPa), 110 mm SDR 11 pipe |
【新闻资讯】查看全部
中矿资源投建高纯锂盐二期项目
2022-03-05 日前,中矿资源集团股份有限公司发布公告称,其全资子公司江西春鹏锂业有限责任公司将建设高纯锂盐二期项目,建设规模为3.5万吨/年,总投资约10亿元。 据悉,中矿资源2.5万吨/年 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |