| 牌号简介 About |
|---|
| 概述：FZ-1140-R5是一种40%gf增强的PPS化合物，为暴露在热水或发动机冷却液中的应用提供出色的水解稳定性。颜色：黑色和天然色（棕色） Outline: FZ-1140-R5 is a 40% GF reinforced PPS compound which provides excellent hydrolytic stability for use of applications exposed to hot water or engine coolant. Color: Black and Natural (Brown) |
产品描述 Product Description
颜色：黑色,自然色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级V-0; 耐水解; Hydrolysis stability,V-0
填料：玻璃纤维 40
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.66 | g/cm³ | ASTM D792 |
|
收缩率 Shrinkage rate |
ASTM D955 | ||
|
MD MD |
0.25 | % | ASTM D955 |
|
TD TD |
1.1 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
23℃，24hr 23℃，24hr |
0.020 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
100 | J/m | ASTM D256 |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM D696 | ||
|
MD：-30~90℃ MD：-30~90℃ |
1/℃ | ASTM D696 | |
|
TD：-30~90℃ TD：-30~90℃ |
1/℃ | ASTM D696 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
|||
|
1.6 mm 1.6 mm |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
|||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耐电弧性 Arc resistance |
sec | ASTM D495 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | ASTM D3638 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
0.40 mm 0.40 mm |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
|
M 级 M-level |
ASTM D785 | ||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
泊松比 Poisson's ratio |
|||
|
摩擦系数 friction coefficient |
ASTM D1894 | ||
|
与钢 - 动态 Steel - Dynamic |
ASTM D1894 | ||
|
与钢 - 静态 Steel - Static |
ASTM D1894 | ||
|
断裂弯曲伸长率 Elongation at break and bending |
% | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
3D打印200℃的超低温工程塑料
2015-12-18 据悉，东京大学生产技术研究所的新野俊树教授等运用3D打印机成功对具有150℃以上耐热性的超级工程塑料完成了立体造形。相比切削和注塑成形等现有加工法，达到额80%左右的强度，可进行复杂形状的加工，有利于完成汽车、飞机的发动机周边零部件等对耐高温性有要求的生产。 熔点280℃、耐热性150℃的聚苯硫醚(PPS)和熔点360℃、耐热性200℃的聚醚醚酮(PEEK)成功完成了立体造形。造形方式为树脂粉末照射激光后反复溶解、冷却凝固，搭建立体形状的粉末积层方法。炉内保持200℃，通过 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付