牌号简介 About |
---|
NORYL™ GFN3F resin是 PPE+PS混合物。30%玻璃纤维增强。符合NSF 61,FDA合规性。吸水率低、水解稳定性。尺寸稳定性。适用于流体工程应用,包括泵壳、泵叶轮和水表部件 PPE+PS blend. 30% Glass reinforced. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump housings, pump impellers and water meter components. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.29 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,5.0kg 300℃,5.0kg |
8.7 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,5 kg 300℃,5 kg |
7.82 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.10 to 0.40 | % | 内部方法 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.060 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/2C | ||
-30℃ -30℃ |
kJ/m² | ISO 179/2C | |
23℃ 23℃ |
kJ/m² | ISO 179/2C | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃ 23℃ |
J/m | ASTM D4812 | |
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span |
℃ | ISO 75-2/Af | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
|||
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
耐电弧性 Arc resistance |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
50 mm跨距 50 mm span |
MPa | ASTM D790 | |
100 mm跨距 100 mm span |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
弯曲强度 bending strength |
ASTM D790 | ||
屈服,50 mm跨度 Yield, 50 mm span |
MPa | ASTM D790 | |
屈服,100 mm跨度 Yield, 100 mm span |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
L 级 Level L |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
塑料机械向绿色环保展开是大势所趋
2017-09-11 随着我国塑料机械产业的不断壮大,通过塑料行业的覆盖面和巨大产量,实现塑料机械行业对于可持续发展和科学发展能够做出的一系列重要贡献,体现本行业绿色发展的总体规划和发展趋势。 近几年来,世界上产业发达国家的注塑机生产厂家都在不断进步普通注塑机的功能、质量、辅助设备的配套能力,以及自动化水平。同时大力开发、发展大型注塑机、专用注塑机、反应注塑机和精密注塑机,以满足生产塑料合金、磁性塑料、带嵌件和数码光盘制品的需求。 |
塑料机械向绿色环保展开是大势所趋 伴随着在我国塑料机械产业的持续发展壮大,根据塑胶行业的涉及面和极大生产量,完成塑料机械行业针对可持续性发展和科学研究发展可以作出的一系列关键奉献,反映本行业翠绿色发展的整体规划和发展发展趋势。
近年来,全世界产业发展国家的注塑机生产商都会不断发展一般注塑机的作用、品质、輔助机器设备的配套设施工作能力,及其自动化技术水准。另外全力开发设计、发展大中型注塑机、专用型注塑机、反映注塑机和精细注塑机,以考虑生产制造塑料合金、带磁塑胶、带镶件和数码光碟产品的要求。 伴随着中国经济发展总体平稳不断身心健康发展,我国塑料机械产业历经十五完成了坚持创新驱动的发展,产业经营规模扩张,持续八年关键经济数据逐渐增长,其发展速度所作关键经济数据在机械设备产业管辖的194个行业中,遥遥领先。 另外,加强产业链系统软件意识,将塑料机械向上下游石油化工产业、中下游产品制造业拓宽,把塑料机械做为新型材料产业链中关键的一环,进而与国家重特大要求、高端装备制造转型发展紧密联系起來,解决塑料机械行业的相对性劣势影响力。 除此之外,国家假如能将塑料机械同数控车床一样做为工业生产的基本机械设备(塑料机械生产加工纤维材料,机床加工金属复合材料),做为国家武器装备工业生产的关键构成部分,对优秀的塑料机械给与像数控车床一样的重点适用和政策优惠,以促进塑料机械行业充分发挥更为显著的杠杆效应,为在我国武器装备工业生产的发展做出更高奉献。 塑料机械工业生产的发展,要融合我国基本国情和目前行业的基本具体,提升关系,便是将塑料机械与加工制造业高档关联,向经济效益产业求发展,与危害社会经济的关键产业和老百姓日常生活密切相关的实际要求关联,凸显塑料机械在加工制造业中的关键母机影响力。 来源于:环球塑化网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
- NORYL树脂光伏接线盒
- 2022-10-18 0
- NORYL树脂具有优秀的尺寸稳定性、电气和热性能,能耐受-40°C至140°C的温度,长期在户外的湿热环境使用后,还可保持85%以上的性能,且具有低翘曲特性,满足对接线盒材料的高要求