牌号简介 About |
---|
玻璃纤维增强的间苯二甲酸二烯丙酯模塑料,具有良好的机械强度,在湿热条件下具有高的电绝缘性能,即使在恶劣环境条件下也具有优异的尺寸稳定性。主要用途:连接器、线轴、电位器、开关。本产品满足重金属和PCA的允许上限,也符合欧盟指令2002/95(RoHS)、2002/96(WEEE)和2006/122(PFOS)的要求。 Glass-fibre reinforced diallyl isophthalate moulding compound Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensional stability even under severe environmental conditions Primary application(s): Connectors, bobbins, potentiometers, switches This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.80 到 2.00 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.70 到 0.85 | g/cm³ | ISO 60 |
收缩率 Shrinkage rate 2 |
|||
MD MD 2 |
0.20 到 0.45 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 0.20 | % | ISO 62 |
后收缩 Post contraction 3 |
< 0.050 | % | ISO 2577 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
注塑成型 injection molding |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
注塑成型 injection molding |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
注塑成型 injection molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
注塑成型 injection molding |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
注塑成型 injection molding |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
注塑成型 injection molding |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:50~100℃ MD:50~100℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1461 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc resistance |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Injection Molded |
3 168 h / 110°C |
【新闻资讯】查看全部
塑料垃圾要挟香港陆地环境
2016-11-04 世界自然基金会香港分会近日发布调查报告称,香港拥有丰富的海岸及海洋生物多样性,但海洋环境却长期受到海洋垃圾的困扰,而海洋垃圾有六至八成是塑料制品。 世界自然基金会香港分会与合作伙伴于2014年6月起展开为期两年的“育养海岸”计划,通过海洋垃圾及生态调查追溯垃圾源头。此计划在香港34处海岸点收集数据。 调查显示,塑料垃圾在岸上大型和小型垃圾中所占比重分别达到六成半和七成半,在沿岸水域漂浮垃圾中占比高达83.7%。在海底垃圾中,塑料垃圾占比六成半,每百米样线收集 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |