牌号简介 About |
---|
FA3227是一种通过高压工艺生产的低密度聚乙烯。FA3227是一种低密度聚乙烯薄膜挤出,紫外线稳定。该等级适用于建筑和建筑薄膜,并符合北欧国家建筑标准中所述的耐热、耐碱和抗紫外线要求。基于FA3227的150微米薄膜的使用寿命至少是相同厚度的非稳定薄膜的4倍。 FA3227 is a low density polyethylene produced in a high-pressure process. FA3227 is a Low Density Polyethylene for Film Extrusion, UV stabilised. This grade is suitable for building and construction film and meets the requirements for heat, alkali and UV resistance described in the building standards from the Nordic countries. A 150-micron film based upon FA3227 will last at least four times as long as an unstabilised film of the same thickness. CAS-No.: 9002-88-4 Applications FA3227 has been developed especially for applications like: Construction films Shrink film Heavy-duty sack Liners Additives FA3227 is UV stabilised. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.922 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.30 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态 With oneself - dynamic |
0.60 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
130 | µm | |
膜刺穿能量 Membrane puncture energy |
|||
130 µm 130 µm |
5.00 | J | ASTM D5748 |
割线模量 Secant modulus |
|||
TD,130 µm TD,130 µm |
MPa | ASTM D882A | |
MD,130 µm MD,130 µm |
MPa | ASTM D882A | |
拉伸强度 tensile strength |
ISO 527-3/22 | ||
MD,24℃,130 µm MD,24℃,130 µm |
MPa | ISO 527-3/22 | |
TD,24℃,130 µm TD,24℃,130 µm |
MPa | ISO 527-3/22 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,130 µm MD, fracture, 130 µ m |
% | ISO 527-3 | |
TD,断裂,130 µm TD, fracture, 130 µ m |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
130 µm 130 µm |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
MD:130 µm MD:130 µm |
N | ISO 6383-2 | |
TD:130 µm TD:130 µm |
N | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
开发新材料成塑料机械行业将来开展趋势
2016-09-27 相对于金属、石材、木材,塑料具有成本低、可塑性强等优点,在国民经济中应用广泛,塑料工业在当今世界上占有极为重要的地位,多年来塑料制品的生产在世界各地高速发展。中国塑料制品产量在世界排名中始终位于前列,其中多种塑料制品产量已经位于全球首位,中国已经成为世界塑料制品生产大国。近年来,面对石油资源逐渐减少的威胁,为了减少塑料工业对传统石化基资源的依赖,开发各种新材料被看作是未来塑料工业发展的必然趋势。 开发新材料成塑料机械行业未来发展趋势 美国应用材料公司是为电子 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |