牌号简介 About |
---|
无筋等级具有丰富的强度和柔韧性,具有很强的抗脆性。UL认证的慢燃(94HB)和自熄等级(94V-0,V-2)存在,所展示的电气性能是任何热塑性塑料中最高的。表现出低吸水性,即使在温度和湿度变化很大的情况下,在长时间的使用中仍保持良好的电性能(CTI和GWIT)。成型产品表面光滑,摩擦系数低,由于起泡量低,PBT适用于要求摩擦磨损性能的场合。该材料非常可靠,使用中的尺寸变化小,具有优异的成型稳定性和尺寸精度。长期的耐化学性是很特殊的,而且在室温下,之后的性能几乎没有退化。未加筋和加筋钢种都表现出优异的流动性和加工性。应用:VCD驱动框架连接器微调器开关按钮,用于燃气瞬时热水器继电器阻隔干燥器整流器外把手高度传感器外壳门镜保持驱动组件外壳节能灯。 Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning(94HB) and self-extinguishing grades(94V-0,V-2) exist, and electrical properties exhibited are the highest of any thermoplastic. Low water absorption is exhibited, and excellent electrical properties(CTI and GWIT) are retained over extended periods of usages, even with widely varied temperature and humidity conditions. The surface of molded products is smooth, and a low coefficient of friction is exhibited.As the amount of froction is low, PBT is suitable for use in application requiring friction and wear properties. The material is exceptionally reliable, with small in-use dimensional variation, and superior molding stability and dimensional precision. Long-term chemical resistance is exceptional, and at room temperature, there is almost no degradation in properties after. Both unreinforced and reinforced grades exhibit exceptional flowability, and excellent processability. Application:VCD drive frames Connectors Trimmers Switch buttons for gas-fired instantaneous water heaters Relay blocks Driers Rectifiers Outer handles Height sensor cases Door mirror stays Drive component housings Energy saving lamp. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.60 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.40 到 0.60 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.050 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
115 | MPa | ASTM D638 |
弯曲模量 Bending modulus |
8000 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
kJ/m² | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
2 mm 2 mm |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
2 mm 2 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
50 Hz 50 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
50 Hz 50 Hz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
巴陵石化:树脂部落实包机制管理设备“低老坏”
2016-09-14 巴陵石化环氧树脂事业部落实设备运行包机制,将现场设备卫生责任细化分配到个人,定期“大扫除”,使之成为一种习惯,两年来有效整治了现场管理“低、老、坏”现象。 2014年3月,该事业部为降低机泵故障,提高效能,结合经济责任制,编写包机制实施细则,规定动设备及关键机组必须成立包机组,开展包机护理工作;明确5条无故障机组标准:机泵完好、故障停机率小于6‰、无设备事故、开展各项包机活动、活动记录和各项资料齐全;公布“一平、二净、三见、四无、五不缺”包机现场卫生标准,即:场地平整;门窗 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |