| 牌号简介 About |
|---|
| 高性能热塑性材料、无增强聚醚酮（PEK）、半结晶、注射成型用深度过滤颗粒、易流动、符合FDA食品接触标准、颜色自然/米色。适用于高强度、高刚度以及高温下良好的延展性。耐腐蚀环境的化学性，适用于医疗和食品接触应用。 High performance thermoplastic material, unreinforced PolyEtherKetone (PEK), semi crystalline, depth filtered granules for injection moulding, easy flow, FDA food contact compliant, colour natural/beige. Applications for high strength and stiffness as well as good ductility at higher temperatures. Chemically resistant to aggressive environments, suitable for sterilsation for medical and food contact applications. |
产品描述 Product Description
用途：医疗/护理用品;非特定食品应用;
颜色：自然色,米黄色
加工条件：注射成型 Injection Molding
性能特点： 半结晶; 机械强度好; 耐化学性; 易消毒; 机械强度好-延展; 食品接触; 易流动; Good liquidity,Good disinfection,Hypocrystalline,Solvent resistance,Food contact compliance,Good Rigidity,Ductility
| 技术参数 Technical Data | |||
|---|---|---|---|
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness Shore hardness |
|||
|
邵氏 D，23℃ Shore D, 23 ℃ |
86 | ISO 868 | |
|
拉伸模量 Tensile Modulus Tensile Modulus |
|||
|
23℃ 23℃ |
4300 | MPa | ISO 527-2 |
|
拉伸强度 Tensile Strength Tensile Strength |
|||
|
屈服 yld，23℃ Yield yld, 23 ℃ |
115 | MPa | ISO 527-2 |
|
拉伸应变 Tensile Strain Tensile Strain |
|||
|
断裂 brk，23℃ Broken BRK, 23 ℃ |
25 | % | ISO 527-2 |
|
弯曲模量 Flexural Modulus Flexural Modulus |
|||
|
23℃ 23℃ |
4000 | MPa | ISO 178 |
|
弯曲强度 Flexural Strength Flexural Strength |
ISO 178 | ||
|
3.50% 应变，23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178 | |
|
23℃ 23℃ |
MPa | ISO 178 | |
|
125℃ 125℃ |
MPa | ISO 178 | |
|
175℃ 175℃ |
MPa | ISO 178 | |
|
275℃ 275℃ |
MPa | ISO 178 | |
|
压缩强度 Compressive Strength Compressive Strength |
ISO 604 | ||
|
23℃ 23℃ |
MPa | ISO 604 | |
|
120℃ 120℃ |
MPa | ISO 604 | |
|
200℃ 200℃ |
MPa | ISO 604 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
ISO 179 | ||
|
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180-A | |
|
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength Izod Unnotched Impact strength of cantilever beam |
|||
|
23℃ 23℃ |
ISO 180 | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT Hot deformation temperature HDT |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
|
玻璃化转变温度 Glass Transition Temperature Glass Transition Temperature |
ISO 11357-2 | ||
|
-- -- |
℃ | ISO 11357-2 | |
|
-- -- |
℃ | ISO 11357-2 | |
|
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
|
TD TD |
ISO 11359-2 | ||
|
< 152℃ < 152℃ |
cm/cm/℃ | ISO 11359-2 | |
|
> 152℃ > 152℃ |
cm/cm/℃ | ISO 11359-2 | |
|
MD MD |
ISO 11359-2 | ||
|
< 152℃ < 152℃ |
cm/cm/℃ | ISO 11359-2 | |
|
> 152℃ > 152℃ |
cm/cm/℃ | ISO 11359-2 | |
|
导热系数 Thermal Conductivity Thermal conductivity |
ISO 22007-4 | ||
|
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
|
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
|
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume Resistivity Volume Resistance |
IEC 60093 | ||
|
23℃ 23℃ |
ohms·cm | IEC 60093 | |
|
125 ℃ 125 ℃ |
ohms·cm | IEC 60093 | |
|
275 ℃ 275 ℃ |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric Strength Dielectric Strength |
|||
|
2 mm 2 mm |
kV/mm | IEC 60243-1 | |
|
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
灼热丝可燃性指数GWFI Glow Wire Flammability Index GWFI |
|||
|
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
|
极限氧指数 Oxygen Index Oxygen Index |
ISO 4589-2 | ||
|
-- -- |
% | ISO 4589-2 | |
|
-- -- |
% | ISO 4589-2 | |
|
毒性 toxicity Toxicity |
NES 713 | ||
|
CO Content CO Content |
NES 713 | ||
|
CO2 Content CO2 Content |
NES 713 | ||
|
Total Gases Total Gases |
NES 713 | ||
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density Density |
g/cm³ | ISO 1183 | |
|
螺旋流动长度 spiral flow length Spiral flow length |
cm | Internal Method | |
|
成型收缩率 Molding Shrinkage Molding shrinkage |
ISO 294-4 | ||
|
TD TD |
% | ISO 294-4 | |
|
MD MD |
% | ISO 294-4 | |
|
吸水率 Water Absorption Water Absorption |
|||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
饱和，100℃ Saturation, 100 ℃ |
% | ISO 62 | |
|
表观粘度 Apparent viscosity Apparent viscosity |
|||
|
400℃ 400℃ |
Pa·s | ISO 11443 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Crystalline |
| 3 模具温度: 392°F, 熔体温度: 743°F |
| 4 1 mm |
| 5 395°C nozzle, 200°C tool |
| 6 At yield |
| 7 Onset |
| 8 Midpoint |
| 9 Average |
| 10 Along flow |
| 11 0.4 mm |
| 12 3.2 mm |
|
【新闻资讯】查看全部 
中国新型TPE资料将成为塑料企业开展方向
2017-07-19 伴随着低碳经济的时代到来，针对一些传统的材料以及工艺已不能满足发展要求，既节能环保、轻量化越来越成为TPE塑料企业所关注的热点，新型TPE材料势必将成为塑料企业的发展方向。TPE作为一种既节能又环保的新型弹性体材料，在未来的发展的前景是非常好。 据了解，亚太地区一直是TPE的最大市场，将占全球需求的近一半。从总的数量上看，中国是世界上最大的TPE消费国，其需求也将继续持续的增长。相比于2007~2012年经济衰退期来看，北美和西欧的TPE需求将显著的改善。对于世界其他地区的 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付