牌号简介 About |
---|
YUCLAIR® MB509U是一种分子量分布较广、熔融指数较低的中密度聚乙烯树脂,0.33g/10min,具有很高的耐低温冲击性、抗应力开裂性和韧性,并具有良好的加工性能。MB509U含有紫外线稳定剂,用于需要户外耐候性的产品。 YUCLAIR MB509U is medium density polyethylene resin with broad molecular weight distribution and relatively low melt index of 0.33 g/10min. It offers a high degree of cold temperature impact resistance, stress crack resistance and toughness combined with good processability. MB509U contains UV-stabilizer, for use in products requiring out-door weathering resistance. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.939 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.35 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
> 1000 | hr | ASTM D1693 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
无断裂 | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
< -80.0 | ℃ | ASTM D746 |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ | ASTM D2117 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
帝斯曼发布新战略
2018-07-02 全球科学公司荷兰皇家帝斯曼集团近日在资本市场日(英国伦敦)上宣布,公司战略更新为:“增长与价值-目标导向,绩效驱动(Growth & Value-Purposeled,Performance driven)”。< |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |