牌号简介 About |
---|
适用于铸造拉伸膜、层压膜、电线和电缆,以及一般用途的膜应用。特点:强度高,韧性好,易加工透明铸膜。也适用于电线电缆及高强度吹膜,防滑,加工性能优异。为了提高透明度,建议与低密度聚乙烯混合。 Applications: For cast stretch film, lamination film, wire and cable, and general purpose film applications. Characteristics: High Strength, tough, and easy processability transparent cast film. Also used for wire and cable and high strength blown film, non-- slip with excellent processability. For higher transparency, blending with LDPE is recommended. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.921 | g/cm³ | ASTM D792-A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.2 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
静态 static state |
> 0.51 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test 2 |
20 | µm | |
测试 test 3 |
30 | µm | |
割线模量 - 1% 正割,MD Secant modulus -1% secant, MD |
ASTM D882 | ||
-- -- 3 |
MPa | ASTM D882 | |
-- -- 2 |
MPa | ASTM D882 | |
割线模量 - 1% 正割,TD Secant modulus -1% secant, TD |
ASTM D882 | ||
-- -- 2 |
MPa | ASTM D882 | |
-- -- 3 |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,吹塑薄膜 MD, fracture, blow molded film |
MPa | ASTM D882 | |
MD,断裂,挤塑薄膜 MD, fracture, extruded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
TD,断裂,吹塑薄膜 TD, fracture, blow molded film |
MPa | ASTM D882 | |
断裂,挤塑薄膜 Fracture, extruded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,吹塑薄膜 MD, fracture, blow molded film |
% | ASTM D882 | |
MD,断裂,挤塑薄膜 MD, fracture, extruded film |
% | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
TD,断裂,吹塑薄膜 TD, fracture, blow molded film |
% | ASTM D882 | |
TD,断裂,挤塑薄膜 TD, fracture, extruded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
ASTM D1709 | ||
铸造薄膜 Casting thin film |
g | ASTM D1709 | |
吹塑薄膜 Blown film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 - MD Elmandorf Tear Strength - MD |
ASTM D1922 | ||
铸造薄膜 Casting thin film |
g | ASTM D1922 | |
吹塑薄膜 Blown film |
g | ASTM D1922 | |
撕裂强度 tear strength |
ASTM D1922 | ||
TD,铸造薄膜 TD, cast thin film |
g | ASTM D1922 | |
TD,吹塑薄膜 TD, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | DSC | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D2457 | ||
45°,吹塑薄膜 45 °, blow molded film |
ASTM D2457 | ||
45°,铸造薄膜 45 °, cast thin film |
ASTM D2457 | ||
雾度 Haze |
ASTM D1003 | ||
铸造薄膜 Casting thin film |
% | ASTM D1003 | |
吹塑薄膜 Blown film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Cast |
3 Blown |
【新闻资讯】查看全部
从“汽车轻量化”看工程塑料在汽车行业的运用
2016-08-26 导读 汽车轻量化已经成为汽车行业的一大趋势,在确保稳定提升性能的基础上,节能化设计各总成零部件,持续优化车型谱。 汽车轻量化的潮流 汽车的轻量化,就是在保证汽车的强度和安全性能的前提下,尽可能地降低汽车的整备质量,从而提高汽车的动力性,减少燃料消耗,降低排气污染。实验证明,汽车质量降低一半,燃料消耗也会降低将近一半。若汽车整车重量降低10%,燃油效率可提高6%-8%;汽车整备 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |