牌号简介 About |
---|
Eltex® PF6912AA是一种在欧洲生产的茂金属LLDPE树脂,其优点和特点是Eltex® PF6912AA是一种含有己烯-1作为共聚单体的聚乙烯共聚物,用茂金属催化剂生产。它具有以下特性:高刚度、优异的抗蠕变性能、抗冲击性和刚度之间的良好平衡、很好的气泡稳定性和吹塑薄膜挤出过程中的易挤出性、良好的光学性能、极低的堵塞性、Eltex® PF6912AA是用抗氧化剂配制而成的。应用Eltex® PF6912AA已开发用于共挤吹塑薄膜结构,特别适用于食品包装、卫生或工业应用。它在刚度、韧性和光学性能之间的独特平衡使其成为最先进的薄膜成分的首选材料,具有最佳的厚度减小。 Eltex® PF6912AA is a metallocene LLDPE resin produced in Europe Benefits & Features Eltex® PF6912AA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties: High stiffness Superior creep resistance Excellent balance between impact resistance and rigidity Very good bubble stability and easy extrudability during blown film extrusion Good optical properties Very low blocking Eltex® PF6912AA is formulated with antioxidants. Applications Eltex® PF6912AA has been developed for use in coextruded blown film structures particularly suitable for food packaging, hygiene or industrial applications. Its unique balance between stiffness, toughness and optical properties makes it the material of choice for the most advanced film compositions with an optimum thickness reduction. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.936 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.2 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
400 | MPa | ISO 527-3 |
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
450 | MPa | ISO 527-3 |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:25 µm,吹塑薄膜 MD: 25 µ m, blow molded film |
g | ASTM D1922 | |
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
伊朗顶级核专家被刺杀后,国际油价将如何反应?
2020-12-02 搜料网资讯: 这几天,伊朗核科学家被暗杀的消息震惊全球,从年初到年末伊朗可谓一波未平一波又起!如果说2020年之前的每一年都是闯关,那么2020一开年,直接就把难度调成了最高 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |