| 牌号简介 About |
|---|
| Lexan HPS2树脂中/高流量聚碳酸酯。用于医疗设备和医药应用。卫生保健变化管理，生物相容性（ISO10993或USP六级）。ETO、蒸汽、电子束和伽马灭菌。包含模具释放。 Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam and gamma sterilizable. Contains mold release. |
产品描述 Product Description
用途：医疗/护理用品;药物;
加工条件：注射成型 Injection Molding
性能特点： 蒸汽消毒; 生物兼容性; 辐射消毒; 流动性高; 环氧乙烷消毒; 电子束消毒; High liquidity,Steam sterilized,E-beam disinfection,Biocompatible,Radiation disinfection,Ethylene oxide disinfection
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
特定体积 Specific volume |
0.835 | cm³/g | ASTM D792 |
|
密度 Density |
1.19 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
18 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
300℃，1.2 kg 300℃，1.2 kg |
16.0 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.50 to 0.70 | % | 内部方法 |
|
吸水率 Water absorption rate |
ASTM D570 | ||
|
24hr 24hr |
% | ASTM D570 | |
|
平衡，23℃ Equilibrium, 23 ℃ |
% | ASTM D570 | |
|
平衡，100℃ Equilibrium, 100 ℃ |
% | ASTM D570 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ 7 |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/2C | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 7 |
ISO 179/1eU | ||
|
-30℃ -30℃ |
ISO 179/1eU | ||
|
23℃ 23℃ |
ISO 179/1eU | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
23℃ 23℃ 8 |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
J/m | ASTM D4812 | |
|
Colors Colors |
J/m | ASTM D256 | |
|
Natural，Tints Natural，Tints |
J/m | ASTM D256 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
ISO 180/1U | ||
|
-30℃ -30℃ |
ISO 180/1U | ||
|
23℃ 23℃ |
ISO 180/1U | ||
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Energy at Peak Load 23℃，Energy at Peak Load |
J | ASTM D3763 | |
|
落锤冲击 Drop hammer impact |
|||
|
23℃ 23℃ |
J | ASTM D3029 | |
|
拉伸冲击强度 Tensile impact strength 9 |
kJ/m² | ASTM D1822 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature 10 |
|||
|
1.8 MPa，未退火，6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，100 mm跨距 1.8 MPa, unannealed, 100 mm span 10 |
℃ | ISO 75-2/Ae | |
|
0.45 MPa，未退火，6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，100 mm跨距 0.45 MPa, unannealed, 100 mm span 10 |
℃ | ISO 75-2/Be | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306 | |
|
B120 B120 |
℃ | ISO 306/B120 | |
|
球压测试 Ball pressure test |
|||
|
125℃ 125℃ |
IEC 60695-10-2 | ||
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：23~80℃ MD：23~80℃ |
1/℃ | ISO 11359-2 | |
|
MD：-40~95℃ MD：-40~95℃ |
1/℃ | ASTM E831 | |
|
比热 specific heat |
J/kg/℃ | ASTM C351 | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ISO 8302 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
|||
|
3.2 mm，在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
|
3.2 mm，在油中 3.2 mm in oil |
kV/mm | IEC 60243-1 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
相对电容率 Relative permittivity |
IEC 60250 | ||
|
50 Hz 50 Hz |
IEC 60250 | ||
|
60 Hz 60 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
IEC 60250 | ||
|
50 Hz 50 Hz |
IEC 60250 | ||
|
60 Hz 60 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
折射率 Refractive index |
ASTM D542 | ||
|
透光率 Transmittance |
|||
|
2540 µm 2540 µm |
% | ASTM D1003 | |
|
雾度 Haze |
|||
|
2540 µm 2540 µm |
% | ASTM D1003 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength 3 |
|||
|
断裂 fracture 3 |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
屈服 yield 3 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 3 |
|||
|
断裂 fracture |
% | ISO 527-2/50 | |
|
断裂 fracture 4 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
屈服 yield 3 |
% | ASTM D638 | |
|
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
|
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
|
弯曲强度 bending strength 4 |
|||
|
屈服，50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
|
泰伯耐磨性 Taber abraser |
|||
|
1000 周期，1000 g，CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | ASTM D1044 | |
|
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
|
M 级 M-level |
ASTM D785 | ||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2,0 in/min |
| 3 类型 1, 2,0 in/min |
| 4 0,051 in/min |
| 5 0,079 in/min |
| 6 Yield |
| 7 80*10*4 sp=62mm |
| 8 80*10*4 |
| 9 Type S |
| 10 120*10*4 mm |
|