牌号简介 About |
---|
OXPEKK® MG240C是一种聚醚酮酮 (PEKK)材料,含有的填充物为40% 碳纤维增强材料。 该产品在北美洲或欧洲有供货,。 OXPEKK® MG240C的典型应用领域为:医疗/保健 OXPEKK® MG240C is a Polyetherketoneketone (PEKK) material filled with 40% carbon fiber. It is available in Europe or North America. Typical application of OXPEKK® MG240C: Medical/Healthcare |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.47 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.050 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
< 0.030 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
3500 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
断裂 fracture |
269 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
熔融温度 Melting temperature |
℃ | DSC | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
巴斯夫双组分聚氨酯经过50小时雨水冲刷测试
2016-06-17 巴斯夫推出的转子叶片专用涂料,最近通过了丹麦的著名研究所50小时的雨水冲刷测试,结果表现优于其他耐雨水冲刷涂料。 据巴斯夫称,考虑到叶片顶端最高达每小时300公里的速度及巨大的压力,高保护涂层是必要的。此外,巴斯夫还断言,天气的影响,例如雨,雪,冰雹,风沙,高温和紫外线辐射,都会损耗叶片,招致频繁的维修和维护周期。 最近试验表明,高达160米/秒(大约570公里/小时)速度的雨对涂层未造成显著损坏。 该公司表示,基于无溶剂,双组分聚氨酯化合物 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |