牌号简介 About |
---|
高分子量高密度聚乙烯(HMW-HDPE)的特点Kpol Chem-K-02/957B是一种采用双峰技术生产的高密度聚乙烯,冷混,为分段最终注射和挤出而开发。一般应用于注塑件,具有较高的机械强度,具有不同的性能。 High Molecular Weight High Density Polyethylene (HMW-HDPE) Characteristics The KPOL Chem - K-02/957B is a high density polyethylene produced with bimodal technology, cold mixture, developed for the segment Eventually Injection and Extrusion. Applications Injection parts in General, with high mechanical strength, with Differentiated Properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.957 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.20 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
14 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
40.0 | MPa | ASTM D882 |
TD,屈服 TD, yield |
30.0 | MPa | ASTM D882 |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD MD |
g | ASTM D1922 | |
TD TD |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | DSC |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
杜邦交通与工业事业部宣布调高Crastin® PBT及Hytrel®产品售价
2020-12-12 搜料网资讯: 2020年12月7日,杜邦交通与工业事业部宣布将自2021年1月1日起或在合同条款允许情况下,在北美、南美、欧洲、亚太区范围内调高杜邦部分产品的售价。 调高杜邦TM Crasti |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |