高性能热塑性材料,30%玻璃纤维增强聚醚醚酮(PEEK),半结晶,注射成型颗粒,非常容易流动,符合FDA食品接触标准,颜色自然/米色。在静态系统中需要更高强度的情况下,具有更薄横截面或更长流动长度的复杂几何体。热膨胀系数低。耐腐蚀环境的化学性,适用于医疗和食品接触应用的灭菌。 High performance thermoplastic material, 30% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food contact compliant, colour natural/beige. Complex geometries with thinner cross sections or longer flow lengths where higher strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
23℃ 23℃ |
7.5 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
45 | kJ/m² | ISO 179/1U |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
23℃ 23℃ |
10 | kJ/m² | ISO 180-A |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength Izod Unnotched Impact strength of cantilever beam |
|||
23℃ 23℃ |
45 | kJ/m² | ISO 180 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
335 | ℃ | ISO 75-2/Af |
玻璃化转变温度 Glass Transition Temperature Glass Transition Temperature |
℃ | ISO 11357 | |
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
ISO 11359-2 | ||
MD:< 143℃ MD:< 143℃ |
1/℃ | ISO 11359-2 | |
MD:> 143℃ MD:> 143℃ |
1/℃ | ISO 11359-2 | |
TD:< 143℃ TD:< 143℃ |
1/℃ | ISO 11359-2 | |
TD:> 143℃ TD:> 143℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal Conductivity Thermal conductivity |
ISO 22007-4 | ||
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
ohms·cm | IEC 60093 | |
介电强度 Dielectric Strength Dielectric Strength |
|||
2 mm 2 mm |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric Constant Dielectric Constant |
|||
23 ℃,1 kHz 23 ℃,1 kHz |
IEC 60250 | ||
耗散因数 Dissipation Factor Dissipation Factor |
|||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数GWFI Glow Wire Flammability Index GWFI |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness Shore hardness |
|||
邵氏 D,23℃ Shore D, 23 ℃ |
ISO 868 | ||
拉伸模量 Tensile Modulus Tensile Modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 Tensile Strength Tensile Strength |
ISO 527-2 | ||
断裂 brk,23℃ Broken BRK, 23 ℃ |
MPa | ISO 527-2 | |
断裂 brk,125℃ Broken BRK, 125 ℃ |
MPa | ISO 527-2 | |
断裂 brk,175℃ Broken BRK, 175 ℃ |
MPa | ISO 527-2 | |
断裂 brk,225℃ Broken BRK, 225 ℃ |
MPa | ISO 527-2 | |
断裂 brk,275℃ Broken BRK, 275 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk,23℃ Broken BRK, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 Flexural Strength Flexural Strength |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
125℃ 125℃ |
MPa | ISO 178 | |
175℃ 175℃ |
MPa | ISO 178 | |
275℃ 275℃ |
MPa | ISO 178 | |
压缩强度 Compressive Strength Compressive Strength |
ISO 604 | ||
23℃ 23℃ |
MPa | ISO 604 | |
120℃ 120℃ |
MPa | ISO 604 | |
250℃ 250℃ |
MPa | ISO 604 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
g/cm³ | ISO 1183 | |
螺旋流动长度 spiral flow length Spiral flow length |
内部方法 | ||
-- -- |
cm | 内部方法 | |
-- -- |
cm | 内部方法 | |
成型收缩率 Molding Shrinkage Molding shrinkage |
ISO 294-4 | ||
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
吸水率 Water Absorption Water Absorption |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
饱和,100℃ Saturation, 100 ℃ |
% | ISO 62 | |
表观粘度 Apparent viscosity Apparent viscosity |
|||
400℃ 400℃ |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Crystalline |
3 1 mm |
4 模具温度: 356°F, 熔体温度: 698°F |
5 模具温度: 392°F, 熔体温度: 752°F |
6 370°C nozzle |
7 Onset |
8 Average |
9 Along flow |
【新闻资讯】查看全部
亚洲第一深水导管架“海基一号”海上安装就位
2022-04-14 4月11日,由海洋石油工程股份有限公司(简称海油工程)负责EPCI(设计、采购、建造、安装)总承包的亚洲第一深水导管架海基一号,在南海东部珠江口盆地海域成功滑移下水并精准就 |
亚洲第一深水导管架“海基一号”海上安装就位 4月11日,由海洋石油工程股份有限公司(简称海油工程)负责EPCI(设计、采购、建造、安装)总承包的亚洲第一深水导管架“海基一号”,在南海东部珠江口盆地海域成功滑移下水并精准就位,创造了亚洲深水导管架海上安装新纪录,标志着我国深水超大型导管架成套关键技术和安装能力达到世界一流水平,对推动海上油气增储上产、保障国家能源安全具有重要战略意义。 “海基一号”总高度达302米,与埃菲尔铁塔高度接近,在全球排名前十。其总重量达3万吨,所用钢材可制造1艘中型航空母舰。下水作业地点距离香港东南200多公里,水深约284米,是国内首次在近300米水深海域安装固定式导管架。 导管架平台是全球应用最广泛的海洋油气生产设施,导管架相当于“基座”,将巨大的平台托举在海面上。由于“海基一号”的吨位超过世界最大浮式起重船的吊装能力,此次海上安装采用滑移下水方式进行。这种方式是利用导管架自身重力并配合液压千斤顶助推,使导管架从驳船平稳地滑入海中,再通过起重船将导管架吊装扶正坐底,从而实现安装就位。 中国海油工程建设部副总经理刘义勇介绍说,中国海油调配国内优势资源,投入亚洲最大下水驳船“海洋石油229”、亚洲第二大单吊起重船“蓝鲸”号等顶级海洋工程船舶,首创“三艘主作业船”联合作业模式,创新应用“运输姿态监测系统”和“下水运动监测系统”,攻克带压注水、水下灌浆、海床存在沙坡沙脊等多项技术难题,确保“海基一号”精准安装就位。 “‘海基一号’是按照百年一遇的恶劣海况进行设计,项目团队攻克南海超强内波流、海底巨型沙波沙脊、万吨级环境荷载、超大型结构物精准下水就位等一系列世界性难题,创新应用深水导管架浮动式下水桁架、超大尺寸X撑结构、封舱隔板设计、大尺度大吨位结构多台吊机联合吊装、适应沙坡沙脊的防沉板方案、数字孪生等十余项新技术,实现深水导管架设计建造技术从基础理论、结构型式、设计理念、施工工艺到运行维护等全方位提升。”海油工程陆丰油田群区域开发工程总包项目经理阳连丰说。 “海基一号”是我国首次尝试300米级深水导管架平台开发模式,与以往类似深水油气田常用的“水下生产系统+浮式生产平台”开发模式相比,更具经济性与安全性,能大幅降低钻完井、工程以及后续的生产操作成本,它的成功应用为经济有效开发我国200米至400米水深海域的油气资源开拓了一条新路。 据悉,“海基一号”将服役于我国陆丰油田群区域开发项目陆丰15-1油田。后续中国海油将进行平台上部组块的安装、调试作业,平台整体建成后将刷新我国海上原油生产平台的重量纪录。陆丰油田群区域开发项目高峰年产原油达185万吨,将为粤港澳大湾区经济社会发展注入新的动力,进一步提高我国能源安全保障能力。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。