牌号简介 About |
---|
Braskem PE SLL318 SLL318是一种线性低密度聚乙烯,丁烯-1共聚物。开发用于铸膜挤出。用该产品制备的薄膜具有良好的力学性能和密封性。它含有抗氧化添加剂。该等级的最低生物基含量为87%,根据ASTM D6866测定。用途:拉伸薄膜;衬里;低密度聚乙烯和高密度聚乙烯(LDPE)的一般用途的混合物和包装;灌溉管道的混合物;中低压交联聚乙烯电线和电缆的绝缘。Braskem PE SLL318描述:SLL318是一种线性低密度聚乙烯,丁烯-1共聚物。开发用于铸膜挤出。用该产品制备的薄膜具有良好的力学性能和密封性。它含有抗氧化添加剂。该等级的最低生物基含量为87%,根据ASTM D6866测定。用途:拉伸薄膜;衬垫;普通用途的低密度聚乙烯和高密度聚乙烯混合物和包装。其他应用:灌溉管道混合物;中低压交联聚乙烯电线电缆绝缘。工艺:薄膜挤出的推荐工艺条件约为170-210°C。最佳工艺条件将根据所用设备的类型而变化,不能作为性能保证。 Braskem PE SLL318 SLL318 is a Linear Low Density Polyethylene developed for cast film extrusion. Films obtained with this product show good mechanical properties and enhanced sealability. It contains antioxidant additives. The minimum biobased content of this grade is 87%, determined according to ASTM D6866. Applications: Stretch films; liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes; insulation for low and medium tension XLPE wires and cables. Process: Recommended processing conditions for film extrusion about 170 - 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. Braskem PE SLL318 SLL318 is a Linear Low Density Polyethylene developed for cast film extrusion. Films obtained with this product show good mechanical properties and enhanced sealability. It contains antioxidant additives. The minimum biobased content of this grade is 87%, determined according to ASTM D6866. Applications: Stretch films; liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes; insulation for low and medium tension XLPE wires and cables. Process: Recommended processing conditions for film extrusion about 170 - 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. Braskem PE SLL318 SLL318 is a Linear Low Density Polyethylene developed for cast film extrusion. Films obtained with this product show good mechanical properties and enhanced sealability. It contains antioxidant additives. The minimum biobased content of this grade is 87%, determined according to ASTM D6866. Applications: Stretch films; liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes; insulation for low and medium tension XLPE wires and cables. Process: Recommended processing conditions for film extrusion about 170 - 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.7 | g/10min | ASTM D1238 |
Biobased Content Biobased Content |
87 | % | ASTM D6866 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
30.0 | MPa | ASTM D882 |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
30.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
弯曲模量 Bending modulus |
|||
1% 正割,TD,38 µm,吹塑薄膜 1% secant, TD, 38 µ m, blow molded film |
MPa | ASTM D790 | |
1% 正割,MD,38 µm,吹塑薄膜 1% secant, MD, 38 µ m, blow molded film |
MPa | ASTM D790 | |
落锤冲击 Drop hammer impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D1709 | |
撕裂强度 tear strength |
|||
MD,38 µm,吹塑薄膜 MD, 38 µ m, blow molded film |
g | ASTM D1922 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
TD,38 µm,吹塑薄膜 TD, 38 µ m, blow molded film |
g | ASTM D1922 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
河北省东光县塑料包装产业标准提升攻坚战片面开启
2016-03-29 日前,在河北省东光县千盛源大酒店,一场塑料包装行业的百企盛会已拉开帷幕。这既是一场推进东光县塑料包装行业发展的研讨会,同样也是一场为东光县争创第二个“知名品牌示范区”的动员会。县质监局、县公安局、工商局、工信局等12家单位、媒体及百余家塑包企业参加会议,副县长刘志松及市、县质监局领导发表重要讲话。 会议全面分析了东光县塑料包装行业的市场状况,提出面对经济新常态,产业区百家企业要牢牢抓住京津冀协同发展的良好机遇,勇于担当、创新突破、合作共赢。 河北百力塑包有限 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |