牌号简介 About |
---|
Lexan FST9405T树脂Lexan*FST9405T树脂是一种高流动性PC共聚物树脂,适用于注塑成型。这种无卤阻燃树脂符合OSU55/55和FAR25.583标准,是飞机内部应用的理想选择。提供不透明颜色。 Lexan* FST9405T resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is OSU55/55 and FAR25.583 compliant and an ideal candidate foraircraft interior applications. Available in opaque colors. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PC Polycarbonate
用途:飞机内饰;
颜色:不透明
加工条件:注射成型 Injection Molding
性能特点: 无卤; 共聚物; 阻燃; 流动性高; High liquidity,Halogen free,Flame Characteristics,Copolymer
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.33 | g/cm³ | ASTM D792 |
密度 Density |
1.33 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
9.0 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
10.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD TD |
0.50 to 0.70 | % | 内部方法 |
MD MD |
% | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ 7 |
ISO 179/1eA | ||
-30℃ -30℃ 8 |
ISO 179/1eA | ||
23℃ 23℃ 8 |
ISO 179/1eA | ||
23℃ 23℃ 7 |
ISO 179/1eA | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ 7 |
ISO 179/1eU | ||
-30℃ -30℃ 8 |
ISO 179/1eU | ||
23℃ 23℃ 8 |
ISO 179/1eU | ||
23℃ 23℃ 7 |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ 9 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 10 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 9 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 10 |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 11 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 11 |
℃ | ISO 75-2/Bf | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 12 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
NBS烟雾密度 NBS smoke density |
|||
Flaming,Dmax Flaming,Dmax |
ASTM E662 | ||
OSU峰值放热速率 OSU peak heat release rate 13 |
kW/m² | FAR 25.853 | |
OSU总放热量 OSU total heat release 14 |
kW·min/m² | FAR 25.853 | |
垂直燃烧测试 Vertical combustion test |
|||
Test a,60 s,passes at Test a,60 s,passes at |
sec | FAR 25.853 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*3 sp=62mm |
8 80*10*4 sp=62mm |
9 80*10*4 |
10 80*10*3 |
11 80*10*4 mm |
12 标准 B (120°C/h), 载荷2 (50N) |
13 5 minute test |
14 2 minute test |
【新闻资讯】查看全部
海南精细化工二期工程丙烯腈项目最新进展
2021-05-25 搜料网资讯: 近日 , 记者走进东方临港产业园看到,多个项目正在加快建设。在海南精细化工二期工程丙烯腈项目(以下简称丙烯腈项目)现场,工人们正顶着烈日,加紧施工,努力 |
海南精细化工二期工程丙烯腈项目最新进展 搜料网资讯:近日,记者走进东方临港产业园看到,多个项目正在加快建设。在海南精细化工二期工程丙烯腈项目(以下简称丙烯腈项目)现场,工人们正顶着烈日,加紧施工,努力确保项目如期竣工投产。 “目前反应器罐体的焊接已经开始,比计划略有提前。”丙烯腈项目综合管理部经理周澍说,该项目的环形道路施工、桩基施工及罐体和反应器的基础施工都已完成,管沟和管网的施工进度均已超过70%。 项目业主和施工单位科学合理安排工人上下班时间,采取错峰、分批施工等措施,开展“奋战六十天、基础出地面”活动,力争6月30日前完成现场土建和基础施工。 丙烯腈项目副总经理刘喜峰介绍,丙烯腈项目是精细化工项目,技术非常先进,利用海南现有的乙烯产品深加工,可进一步延伸产业链。该项目的建设将给地方税收和经济增长作出贡献。 据了解,目前,丙烯腈项目施工总体进度已达43%,累计完成投资超过3.5亿元。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。