SABIC® PP 525P是一种中等流动材料,通常用于板材和热成型等挤压应用。SABIC® PP 525P通常用于奶制品、花盆、黄色脂肪和一次性盘子和杯子。然而,客户也将此等级与滑石和碳酸钙等填料结合使用。SABICPP 525P是专为(双轴)定向聚丙烯薄膜挤出而开发的,具有非常特殊的分子结构,提供拉伸过程所需的最终性能。SABICP525P通常用于单层或共挤(B)OPP薄膜。SABICP525P以其优异的金属化性能而闻名。本文所述产品尤其未经测试,因此未经验证可用于医药/医疗应用。 SABIC® PP 525P is a medium flow material typically used in extrusion applications like sheet and thermoforming. SABIC® PP 525P is typically used in dairy, flower pots, yellow fats and disposables plates and cups. However, customers use this grade also in combination with fillers like Talc and CaCO3. SABIC®PP 525P is particularly developed for (biaxially) oriented PP film extrusion with a very specific molecular structure providing the ultimate properties required for the stretching process. SABIC®PP 525P is typically used in mono layer or coextruded (B)OPP film. SABIC®PP 525P is known for its excellent metallisation behaviour. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ASTM D792, ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
3.0 | g/10min | ASTM D1238,ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
1% 正割 1% secant 1 |
1550 | MPa | ASTM D638 |
-- -- |
1550 | MPa | ISO 527-2/1A/1 |
拉伸强度 tensile strength |
|||
屈服 yield 2 |
36.0 | MPa | ASTM D638 |
屈服 yield |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/1A/50 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256-A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed 4 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed 5 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525,ISO 306/A120 6 6 | |
B120 B120 |
℃ | ASTM D1525, ISO 306/B120 7 7 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.039 in/min |
3 2.0 in/min |
4 testbar 80*10*4mm |
5 标准 B (120°C/h), 压 力1 (10N) |
6 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
SONGWON 在Chinaplas2017上彰显行业承诺
2017-05-17 韩国蔚山 - 2017年05月16日 - SONGWON 产业集团是全球第二大聚合物稳定剂制造商,其战略目标是成为中国塑料制造业领先的稳定剂供应商,为践行此目标,集团将于今年 5 月 16-19 日参加在中国广州举办的中国国际塑料橡胶工业展览会 (Chinaplas)。 中国国际塑料橡胶工业展览会不仅是亚太地区最大型的塑料和橡胶展览会,业内人士更公认其是世界第二大最具影响力的贸易博览会,仅次于德国杜塞尔多夫国际塑料橡胶工业展览会(简称 K 展)。2017 年中国国际塑料橡胶 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |