公司信息及水印
牌号简介 About |
---|
TEKANATE™ G7020是一种聚碳酸酯(PC)产品,。 它可以通过注射成型进行加工,在亚太地区有供货。 Features G7020 is a unreinforced polycarbonate with MFI 20g/10min. Application E&E Housing and Components Automotive Interior. Drying Product is dried and packed with a moisture content of <0.16%. Should the Packaging become damaged or be left open too long, then the material must be Dried. A too high moisture content can lead to a reduction of optical and Mechanical properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
20 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.60 到 0.80 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
62.5 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
140 | % | ASTM D638 |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
一种复合资料的直升机部件采用3D打印的聚砜(PSU)模具制…
2017-12-11 在Thermwood Corporation公司、Applied Composite Engineering(简称“ACE”)公司、Techmer PM公司以及美国普渡大学复合材料制造与仿真中心的共同努力下,一种复合材料的直升机部件已在一幅3D打印的聚砜(PSU)模具中被生产出来。 采用Techmer PM公司提供的碳纤维增强材料,该模具在Thermwood公司的大型增材制造(简称“LSAM”)设备上被打印出来。利用该3D打 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |