| 牌号简介 About |
|---|
| 符合ISO 1043-1的化学缩写：POM成型化合物ISO 9988-POM-K，M-GNR，04-002，K5 POM共聚物易流动注射成型型，强度、刚度和硬度较高，经特殊粉笔改性；对溶剂、燃料和强碱具有良好的耐化学性，并具有良好的抗水解性；对Rmal和氧化降解；良好的磨损性能，符合UL 94 HB标准，天然厚度超过1.5 mm。厚度大于1 mm时，燃烧速率为ISO 3795和FMVSS 302<100 mm/min。适用范围：适用于无润滑或仅一次润滑的滑动部件和齿轮。fmvss=联邦机动车安全标准（美国）ul=保险商实验室（美国） Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GNR, 04-002, K5 POM copolymer Easy flowing Injection molding type with higher strength, rigidity and hardness with special chalk modified; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation; good wear properties UL- registration in natural and a thickness more than 1.5 mm as UL 94 HB. Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm. Ranges of applications: For unlubricated or once-only-lubricant sliding Parts and gear wheels. FMVSS = Federal Motor Vehicle Safety Standard (USA) UL = Underwriters Laboratories (USA) |
产品描述 Product Description
用途：齿轮;车轮;
性能特点： 防火阻燃等级HB; 机械强度好; 耐磨; 耐化学性; 流动性中等; 耐水解; 耐燃油; 耐碱; Good Rigidity,Alkali resistant,Hydrolysis stability,Moderate liquidity,Good wear resistance,Solvent resistance,Fuel resistance,HB
填料：碳酸钙
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.44 | g/cm³ | ISO 1183 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
190℃，2.16 kg 190℃，2.16 kg |
11.0 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
ISO 294-4 | ||
|
TD TD |
1.8 | % | ISO 294-4 |
|
MD MD |
2.0 | % | ISO 294-4 |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
0.65 | % | ISO 62 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ISO 527-2/1A/50 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
% | ISO 527-2/1A/50 | |
|
标称拉伸断裂应变 Nominal tensile fracture strain |
% | ISO 527-2/1A/50 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
熔融温度 Melting temperature 3 |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
相对电容率 Relative permittivity |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
3.00 mm 3.00 mm |
UL 94 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 10°C/min |
|
【新闻资讯】查看全部 
瑞典专业化学品公司重组业务
2019-01-23 瑞典专业化学品公司Perstorp正在重组业务，以支持未来的增长计划，并加强内部整合。此举将导致56个工作岗位的损失，其中瑞典32个，国外24个。 该公司表示，将把业务重组为三个业务部门：特种多元醇和解决方案、先进化学品和动物营养。此外，它还将把供应链和运营部门合并为一个单位。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付