牌号简介 About |
---|
POLYNIL® P60是一种用于挤出的非增强聚酰胺66(尼龙66)。该2.9粘度聚酰胺66树脂符合FDA标准,并通过NSF-61认证,可接触饮用水。 POLYNIL® P60 is an unreiforced Polyamide 66 (Nylon 66) for extrusion. This 2.9 viscosity Polyamide 66 resin is FDA compliant and is NSF-61 certified for contact with potable water. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | ISO 1183 |
吸水率 Water Absorption |
ISO 62 | ||
23℃,24hr 23℃,24hr |
1.5 | % | ISO 62 |
饱和,23℃ Saturation, 23 ℃ |
8.5 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
3200 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
82.0 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Flexural Modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 Flexural Strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
|||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
连续使用温度 Continuous use temperature 2 |
℃ | IEC 60216 | |
维卡软化温度 Vicat Softening Temperature |
℃ | ISO 306/B | |
球压测试 Ball pressure test |
IEC 60695-10-2 | ||
125℃ 125℃ |
IEC 60695-10-2 | ||
165℃ 165℃ |
IEC 60695-10-2 | ||
熔融温度 Melting temperature |
℃ | ||
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相比漏电起痕指数 Comparative Tracking Index |
|||
3.20 mm,解决方案 A 3.20 mm, solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
灼热丝可燃性指数 Glow Wire Flammability Index(GWFI) |
IEC 60695-2-12 | ||
0.80 mm 0.80 mm |
℃ | IEC 60695-2-12 | |
3.2 mm 3.2 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Glow Wire Ignitability Temperature(GWIT) |
IEC 60695-2-13 | ||
0.8 mm 0.8 mm |
℃ | IEC 60695-2-13 | |
3.2 mm 3.2 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Oxygen Index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 20000 hr |
【新闻资讯】查看全部 ![]()
深圳:挺进创新“深水区”
2022-04-09 从默默无闻的边陲小镇,到具有全球影响力的现代化国际大都市,深圳,被寄予率先突围原始创新难关、抢占全球科技高点的殷殷期望。 科创企业持续攀登原始创新高地,2021年战略性 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |