牌号简介 About |
---|
EMERGE™ PC 8830-5 LT高级树脂是一种透明、耐点燃的PC树脂,不含氯化、溴化或磷基阻燃剂,其设计符合德国标准DIN VDE-0472/第815部分有关卤素的要求。这种树脂结合了良好的机械和耐热性能,确保更长的持续美学和机械阻力的应用。Emerge PC 8830-5LT具有1.0 mm的UL 94 V-0额定值,包含脱模剂和紫外线稳定剂应用LED管、LED灯透镜电气零件。 EMERGE™ PC 8830-5 LT Advanced Resin is a transparent, ignition resistant PC resin that contains no chlorinated or brominated or phosphorous based flame retardant, designed to meet the German norm DIN VDE-0472/Part 815 on halogens. This resin combines good mechanical and heat resistant properties, ensuring longer sustained aesthetics and mechanical resistance to the applications. EMERGE ™ PC 8830-5LT has a UL 94 V-0 rating at 1.0 mm, 5VA @ 3mm and UL746C f1 rating. The material contains mould release agent and UV stabilizer. Applications LED Tube, LED lamp Lens Electrical parts |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ISO 1183/B |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
5.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
0.70 | % | ISO 294-4 |
MD MD |
0.70 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2400 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
ISO 527-2/50 | ||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
MPa | ISO 527-2/50 | |
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
ISO 527-2/50 | ||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
% | ISO 527-2/50 | |
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ISO 306/A120 | |
B50 B50 |
℃ | ISO 306 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.00 mm 1.00 mm 3 |
UL 94 | ||
2.50 mm 2.50 mm 3 |
UL 94 | ||
3.00 mm 3.00 mm 4 |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
1.0 mm 1.0 mm 4 |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm 3 |
℃ | IEC 60695-2-12 | |
2.0 mm 2.0 mm 3 |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm 3 |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire 3 |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
|||
1000 µm 1000 µm |
% | ||
2000 µm 2000 µm |
% |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
3 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
【新闻资讯】查看全部
节后,PVC市场交投清淡
2019-02-12 节后归来,PVC市场交投清淡,受期货上涨影响,部分商家报价跟随走高,但多数业者尚未返市,贸易商报价不多,观望为主。下游尚未开工,市场询盘寥寥,成交量有限。 春节期间,各地成交明显下滑,市场处于休市状态。节前下游备货较为充足,受春节长假影响,目前下游暂未开工,但PVC生产企业装置仍保持较高负荷运行,社会库存也呈小幅增长趋势。2月初至今,PVC企业库存量呈上升阶段,据监测显示,华东、华南市场库存量较节前将有明显增加,预计华东、华南PVC库存总量较节前增加3%左右,PVC生产企业 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |