牌号简介 About |
---|
MARPOL® LL6R 804UV是以己烯为共聚单体的新一代茂金属中密度聚乙烯。这是颗粒形式的天然等级。用于制造旋转模制品的推荐应用 MARPOL® LL6R 804UV is a new generation metallocene medium density polyethylene with hexene as comonomer. This is a natural grade available in pellet form. Recommended Applications Intended for the manufacture of rotomolded items |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
4.0 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
ASTM D1693 | ||
10%非离子洗涤剂,F50 10% non-ionic detergent, F50 |
155 | hr | ASTM D1693 |
100%非离子洗涤剂,F50 100% non-ionic detergent, F50 |
> 900 | hr | ASTM D1693 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
20.7 | MPa | ASTM D638 |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服 yield |
% | ASTM D638 | |
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ | ASTM D3417 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
银行卡是PVC资料做成的么?
2017-08-21 从世界上第一张银行卡发展开始算起,只有短短的一二十年时间,那么伴随着我国的改革开放事业的稳健进行和国民经济的迅速发展,我国的银行卡业绩可以说是突飞猛进、日新月异。随着理念的转变,去银行存钱的人也就越多,这就进一步的促进了银行的业务范围的扩展,同时为银行的发展注入了新的活力。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |