牌号简介 About |
---|
NANCAR® 1082是一种中高丙烯腈橡胶,含有50份邻苯二甲酸二(2-乙基己基)酯(DEHP)。NANCAR® 1082可被视为增塑剂母料,与标准Nancar NBR和其他需要的橡胶一起使用。它具有分散性好、功耗低、节省时间等优点,特别适用于低硬度NBR产品。NANCAR® 1082建议用于软辊、高伸长和低硬度项目。 NANCAR® 1082 is a medium high acrylonitrile rubber included with 50 phr of Di(2-ethylhexyl)phthalate (DEHP). NANCAR® 1082 can be considered as a plasticizer master batch with are used in conjunction with standard NANCAR NBR and other rubbers where the needs demand. It offers outstanding processing characteristics with the advantages of better dispersion, low power consumption and time savings especially for low durometer NBR products. NANCAR® 1082 is recommended for use in soft rollers, high extending and low durometer items. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
门尼粘度 Mooney viscosity |
|||
ML 1+4,100℃ ML 1+4,100℃ |
45 | MU | ASTM D1646 |
丙烯腈含量(Bound) Acrylonitrile content (Bound) |
31.5 | % | 内部方法 |
Stabilizer Stabilizer |
Non-staining | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness 2 |
|||
邵氏 A Shaw's A 2 |
50 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
屈服 yield 2 |
13.7 | MPa | ASTM D412 |
300% 应变 300% strain 3 |
MPa | ASTM D412 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 3 |
% | ASTM D412 | |
压缩形变 Compression deformation 4 |
|||
100℃,70 hr 100℃,70 hr 4 |
% | ASTM D395 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 2 |
|||
100℃,70 hr 100℃,70 hr 2 |
% | ASTM D865 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air 2 |
|||
100℃,70 hr 100℃,70 hr 2 |
% | ASTM D865 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air 2 |
|||
邵氏 A,100℃,70 hr Shore A, 100 ℃, 70 hr 2 |
ASTM D865 | ||
拉伸强度的变化率 The rate of change in tensile strength 2 |
ASTM D471 | ||
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
极限伸长率的变化率 Change rate of ultimate elongation 2 |
ASTM D471 | ||
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
邵氏硬度的变化率 The rate of change in Shore hardness 2 |
ASTM D471 | ||
支撐 A,100℃,70 hr,在ASTM #1油中 Support A, 100 ℃, 70 hr, in ASTM # 1 oil |
ASTM D471 | ||
支撐 A,100℃,70 hr,在ASTM #3油中 Support A, 100 ℃, 70 hr, in ASTM # 3 oil |
ASTM D471 | ||
体积变化 Volume change 2 |
ASTM D471 | ||
100℃,70 hr,ASTM 标准油(1号) 100 ℃, 70 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
100℃,70 hr,ASTM 标准油(3号) 100 ℃, 70 hr, ASTM standard oil (No.3) |
% | ASTM D471 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 硫化 6,00 min 在 320°F |
3 Cured for 6.00 min at 160°C |
4 Cured for 11.0 min at 160°C |
【新闻资讯】查看全部
先达公司天津南港海水淡化综合利用项目正式启动
2021-07-16 搜料网资讯: 2021年7月12日,先达(天津)海水资源开发有限公司天津南港工业区海水淡化及综合利用一体化(30万吨示范)项目在天津南港工业区正式启动。 据介绍,该项目是天津南港 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |