CALIBRE™ 621-2 枝化聚碳酸酯主要应用于大规模的挤出吹塑或者注塑-拉伸吹塑水瓶加工,可使,其他适用的应用也包括电器和片材产品。CALIBRE™ 621-2特殊的流变性能使其在吹塑加工中具有优异的加工性能。优异的加工性能、韧性、光学性能以及符合食品接触法规使得CALIBRE™ 621-2 可以成功地应用于众多领域。 主要特性: 优异的外观 抗冲击性能和耐热性能优异 在吹塑模塑加工过程中具有优异的加工性能 CALIBRE™ 621-2 符合以下法规: 美国食品和药物管理局法规 21 CFR 177.1580 请查询法规以获取完备的细节资料。 应用领域: 吹塑水瓶 电器工业 CALIBRE™ 621-2 branched polycarbonate resin is mainly designed for large extrusion blow molded or injection-stretch blow molded water bottles, however other successful applications do include appliance and sheet molded products. Specific rheological behaviour has been engineered into CALIBRE™ 621-2 to provide excellent processability during blow molding operations. The excellent processability, practical toughness, exceptional optics, and food compliance properties of CALIBRE™ 621-2 enable a host of successful applications. Main Characteristics: Brilliant optical appearance Excellent impact and heat resistance Excellent processability during blow molding operations CALIBRE™ 621-2 should comply with: U.S. FDA 21 CFR 177.1580 Consult the regulations for complete details. Applications: Blow Molded Water Bottles Appliance industry |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
密度 Density |
1.20 | g/cm³ | ISO 1183/B |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
2.0 | g/10min | ISO 1133 |
300℃,1.20kg 300℃,1.20kg |
2.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 to 0.70 | % | ASTM D955 |
MD MD |
% | ISO 294-4 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 2 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 2 |
MPa | ISO 178 | |
弯曲强度 bending strength 2 |
MPa | ASTM D790 | |
弯曲强度 bending strength 2 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | ISO 179-1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180/A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
B50 B50 |
℃ | ISO 306 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.039 in/min |
3 2.0 in/min |
4 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
CHINAPLAS三天累计133,844人入场
2016-04-29 今届CHINAPLAS场面更加火热,三天累计人数已超2014年上海展会。 CHINAPLAS 2016今天是展会最后一天,今天是免费入场,行业人士请把握机会,快快入场。 27日是第三天展会,入场人数为38,757人,海外观众占比27.44%,累计三天人数为133,844。 2014年的上海展会,累计录得入场人数130,370。今届展会三天的入场人数,已超过去年的总人数,真正更上层楼。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |