| 牌号简介 About |
|---|
| CALIBRE™ 300EP-22 聚碳酸酯树脂具有注塑模塑应用所需的优异的抗冲击性能、耐热畸变性能和光学透明度。这些产品所拥有的较高的熔体流动速率可以使其轻易地加工出复杂的零部件。CALIBRE 300 EP-22 系列产品包含有4中添加剂产品类型： CALIBRE 300EP：无脱模剂或者抗紫外线稳定剂。CALIBRE 301EP：含脱模剂。 CALIBRE 302EP：含抗紫外线稳定剂。CALIBRE 303EP：含脱模剂和抗紫外线稳定剂。 政府和业界标准： 加拿大标准协会(CSA)的要求 美国安全检测实验室 (UL)的要求 应用领域： 电器产品 存储介质 电子元器件 光散射器 CALIBRE™ 300EP-22 Series are polycarbonate resins that offer exceptional impact resistance, heat distortion resistance, and optical clarity for injection molding applications. Their high melt flow rate allows complex parts to be easily molded. The CALIBRE 300EP-22 series products are available in 4 additive packages: CALIBRE 300EP: No mold release or UV Stabilizer. CALIBRE 301EP: Mold release. CALIBRE 302EP: UV stabilizer. CALIBRE 303EP: Mold release and UV stabilizer. Govt. and Industry Standards: CSA (Canadian Standards Association) Underwriters Laboratory, Inc. (UL) Applications: Appliances Storage Electrical components Light diffusers |
产品描述 Product Description
用途：电气/电子应用领域;电器用具;
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级V-2; 透光性好; 流动性高; 冲击性能好; Good Clarity,High impact resistance,High liquidity,V-2
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.20 | g/cm³ | ASTM D792 |
|
密度 Density |
1.20 | g/cm³ | ISO 1183/B |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
22 | g/10min | ISO 1133 |
|
300℃，1.20kg 300℃，1.20kg |
22 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.50 to 0.70 | % | ASTM D955 |
|
MD MD |
% | ISO 294-4 | |
|
吸水率 Water absorption rate |
|||
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ASTM D570 | |
|
23℃，24hr 23℃，24hr |
% | ASTM D570 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
kJ/m² | ISO 180-A | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 5 |
|||
|
23℃，Total Energy 23℃，Total Energy 5 |
J | ASTM D3763 | |
|
拉伸冲击强度 Tensile impact strength |
kJ/m² | ASTM D1822 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
|
1.8 MPa，退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
|
0.45 MPa，退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 6 | |
|
B50 B50 |
℃ | ISO 306 | |
|
球压温度 Ball pressure temperature |
℃ | IEC 60335-1 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-40~82℃ MD：-40~82℃ |
1/℃ | ASTM D696 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
|||
|
2.00 mm，解决方案 A 2.00 mm, solution A |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level 5 |
UL 94 | ||
|
1.60 mm 1.60 mm |
UL 94 | ||
|
3.20 mm 3.20 mm |
UL 94 | ||
|
极限氧指数 Extreme oxygen index 7 |
% | ISO 4589-2 | |
|
平均燃烧程度 Average combustion degree |
cm | ASTM D635 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
折射率 Refractive index |
ASTM D542 | ||
|
折射率 Refractive index |
ISO 489 | ||
|
透光率 Transmittance |
% | ASTM D1003 | |
|
雾度 Haze |
% | ASTM D1003 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
|
拉伸强度 tensile strength 2 |
|||
|
断裂 fracture 2 |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
屈服 yield 2 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 2 |
|||
|
断裂 fracture |
% | ISO 527-2/50 | |
|
断裂 fracture 2 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
屈服 yield 2 |
% | ASTM D638 | |
|
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus 4 |
MPa | ISO 178 | |
|
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 4 |
MPa | ISO 178 | |
|
泰伯耐磨性 Taber abraser |
% | ASTM D1044 | |
|
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
|
M 级 M-level |
ASTM D785 | ||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 类型 1, 2.0 in/min |
| 3 方法 I (三点负荷), 类型 1, 0.079 in/min |
| 4 0.079 in/min |
| 5 11.1 ft/sec |
| 6 速率 A (50°C/h), 载荷2 (50N) |
| 7 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
| 8 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
|
【新闻资讯】查看全部 
威格斯VICTREX管路为商用飞机减重45%
2015-12-03 为提升新商用飞机平台的整体燃油效率和可靠性，中国商用飞机有限责任公司(COMAC)选用威格斯管路VICTREX Pipes作为高压电缆导管，替代金属管道。这种全新热塑解决方案最多可减重45%。 这种解决方 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付